Evaluation on High-temperature Adhesion Performance of Hot-applied Sealant for Asphalt Pavement  

作　　者：李峰 LI Tinggang SHI Xiaopei 

机构地区：[1]Key Laboratory of Road Structure & Material,Research Institute of Highway, Ministry of Transport

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2014年第6期1237-1241,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China(Nos.51378242 and 51008146);the Transportation Industry Science and Technology Project of Beijing(No.kj2013-2-14)

摘　　要：In order to investigate the high-temperature performances of the asphalt pavement hot-applied sealant, as well as to reduce failures of the sealant pullout, the softening point test and the flow test（two existing methods for evaluating high-temperature performances） were conducted. It was found that both tests could not accurately reflect the adhesion performances of the sealant at high temperatures. For this purpose, the adhesion test for PSAT（pressure sensitive adhesive tape） has been taken as a reference to develop a device that is suitable for evaluating the adhesion performances, by modifying relevant test parameters according to the road conditions at high temperatures. Thirteen common sealants were tested in the modified adhesion test, softening point test and f low test. The experimental results show that no significant correlation（p〉0.05） exists between the adhesion value, softening point, adhesion value and flow value; while a significant correlation（p〈0.05） exists between the softening point and flow value. The modified adhesion test is efficient in distinguishing the hightemperature adhesion performances of different sealants, and can be used as a standard method for evaluating such performances.In order to investigate the high-temperature performances of the asphalt pavement hot-applied sealant, as well as to reduce failures of the sealant pullout, the softening point test and the flow test（two existing methods for evaluating high-temperature performances） were conducted. It was found that both tests could not accurately reflect the adhesion performances of the sealant at high temperatures. For this purpose, the adhesion test for PSAT（pressure sensitive adhesive tape） has been taken as a reference to develop a device that is suitable for evaluating the adhesion performances, by modifying relevant test parameters according to the road conditions at high temperatures. Thirteen common sealants were tested in the modified adhesion test, softening point test and f low test. The experimental results show that no significant correlation（p〉0.05） exists between the adhesion value, softening point, adhesion value and flow value; while a significant correlation（p〈0.05） exists between the softening point and flow value. The modified adhesion test is efficient in distinguishing the hightemperature adhesion performances of different sealants, and can be used as a standard method for evaluating such performances.

关 键 词：hot-applied sealant pullout high-temperature performance adhesion performance modified adhesion test 