Photorefractive Effect in an Azobenzene Chromophore Side Groups Polymer  

作　　者：方华 LI Mingtian 

机构地区：[1]School of Chemical and Environmental Engineering, Wuhan Polytechnic University [2]College of Materials Science and Chemistry Engineering, Sichuan University of Science and Engineering

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2014年第6期1290-1293,共4页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China(No.51303115)

摘　　要：We have analyzed the photorefractive（PR） effect of a polymer composite was reported which combines a novel bi-functional poly（N-vinyl）-3-[p-nitrophenylazo]carbazolyl（PVNPAK） and 2,4,7-trinitro-9-fluorenone（TNF）. PVNPAK was synthesized by a post-azo-coupling reaction, with an azo derivative as the electrooptic chromophore and carbazolyl as photoconductive moiety. The asymmetric two-beam coupling gain of 13.9 cm-1 and diffraction efficiency of 1.2% for poled polymer film fabricated using a corona poling are obtained at the wavelength of 647.1 nm, confirming photorefractivity. We interpreted this result as the orientational enhancement, in which the spatial charge field may enhance the modulated orientation of the azobenzen chromophore. It is unexpected that the photorefractive gain of 9.5 cm-1 for the unpoled polymer film also was observed without external field in two-beam coupling（TBC） experiment. This phenomenon is attributed to a light-induced orientational grating when the azobenzene groups are illuminated by polarized light.We have analyzed the photorefractive（PR） effect of a polymer composite was reported which combines a novel bi-functional poly（N-vinyl）-3-[p-nitrophenylazo]carbazolyl（PVNPAK） and 2,4,7-trinitro-9-fluorenone（TNF）. PVNPAK was synthesized by a post-azo-coupling reaction, with an azo derivative as the electrooptic chromophore and carbazolyl as photoconductive moiety. The asymmetric two-beam coupling gain of 13.9 cm-1 and diffraction efficiency of 1.2% for poled polymer film fabricated using a corona poling are obtained at the wavelength of 647.1 nm, confirming photorefractivity. We interpreted this result as the orientational enhancement, in which the spatial charge field may enhance the modulated orientation of the azobenzen chromophore. It is unexpected that the photorefractive gain of 9.5 cm-1 for the unpoled polymer film also was observed without external field in two-beam coupling（TBC） experiment. This phenomenon is attributed to a light-induced orientational grating when the azobenzene groups are illuminated by polarized light.

关 键 词：photorefractive （PR） effect poly（N-vinyl）-3-[p-nitrophenylazo]carbazolyl orientational enhancement 

分 类 号：O631.24[理学—高分子化学]