铸造工艺参数对高温合金法兰晶粒度影响  

Effects of Casting Technology Parameter on Grain Size of Superalloy Flange

作　　者：胡德友 孟祥炜[2] 彭艳锋[2] 崇贤博 付利军[2] 肖文丰[2] 李曙光[2] 

机构地区：[1]天津航天长征火箭制造有限公司,天津300450 [2]首都航天机械公司,北京100076

出　　处：《航天制造技术》2014年第6期22-24,28,共4页Aerospace Manufacturing Technology

基　　金：工信部科技重大专项子课题2009ZX04006-042-03资助

摘　　要：采用新型细晶铸造技术，通过合理控制浇注温度和模壳预热温度，研究了铸造工艺对K4202高温合金法兰晶粒度的影响。结果表明，浇注温度1335～1345℃，浇注速度18～25kg/s，模壳预热温度1080～1150℃时，新型细晶铸造技术制备的法兰铸件的微观晶粒度在ASTM4-ASTM6.5级，实现了全截面均匀细等轴晶。For controlling pouring temperature and temperature of mould reasonably by using new casting technology, the effect of casting technology parameter on grain size of superalloy flange is explored. The results show that grain size of flange casting made in new casting technology stays ASTM4-ASTM6.5 when pouring temperature, casting rate, temperature of mould is 1335~1345 ℃, 18~25kg/s and 1080~1150 ℃respectively. At the same time, equal-axis fine crystal-grain is distributed evenly over whole cut off casting.

关 键 词：新型细晶铸造技术 高温合金 晶粒度 

分 类 号：V460[航空宇航科学与技术—航空宇航制造工程] V261.31