Hydration mechanism of low quality fly ash in cement-based materials  

作　　者：刘数华 孔亚宁 王露 

机构地区：[1]State Key Laboratory of Water Resources and Hydropower Engineering Science,Wuhan University [2]Department of Civil Environmental and Geomatic Engineering University College London London WC1E 6BT,UK

出　　处：《Journal of Central South University》2014年第11期4360-4367,共8页中南大学学报（英文版）

基　　金：Project(51208391) supported by the National Natural Science Foundation of China

摘　　要：The hydration mechanism of low quality fly ash in cement-based materials was investigated. The hydration heat of the composite cementitious materials was determined by isothermal calorimetry, and the hydration products, quantity, pore structure and morphology were measured by X-ray diffraction(XRD), thermalgravity-differential thermal analysis(TG-DTA), mercury intrusion porosimetry(MIP) and scanning electron microscopy(SEM), respectively. The results indicate that grinding could not only improve the physical properties of the low quality fly ash on particle effect, but also improve hydration properties of the cementitious system from various aspects compared with raw low quality fly ash(RLFA). At the early stage of hydration, the low quanlity fly ash acts as almost inert material; but then at the later stage, high chemical activity, especially for ground low quality fly ash(GLFA), could be observed. It can accelerate the formation of hydration products containing more chemical bonded water, resulting in higher degree of cement hydration, thus denser microstructure and more reasonable pore size distribution, but the hydration heat in total is reduced. It can also delay the induction period, but the accelerating period is shortened and there is little influence on the second exothermic peak.The hydration mechanism of low quality fly ash in cement-based materials was investigated. The hydration heat of the composite cementitious materials was determined by isothermal calorimetry, and the hydration products, quantity, pore structure and morphology were measured by X-ray diffraction（XRD）, thermalgravity-differential thermal analysis（TG-DTA）, mercury intrusion porosimetry（MIP） and scanning electron microscopy（SEM）, respectively. The results indicate that grinding could not only improve the physical properties of the low quality fly ash on particle effect, but also improve hydration properties of the cementitious system from various aspects compared with raw low quality fly ash（RLFA）. At the early stage of hydration, the low quanlity fly ash acts as almost inert material; but then at the later stage, high chemical activity, especially for ground low quality fly ash（GLFA）, could be observed. It can accelerate the formation of hydration products containing more chemical bonded water, resulting in higher degree of cement hydration, thus denser microstructure and more reasonable pore size distribution, but the hydration heat in total is reduced. It can also delay the induction period, but the accelerating period is shortened and there is little influence on the second exothermic peak.

关 键 词：low quality fly ash cement-based materials hydration products pore structure 

分 类 号：TQ172.44[化学工程—水泥工业]