溶胶-凝胶法制备多晶莫来石连续纤维  

Preparation of Polycrystalline Mullite Continuous Fibers by Sol-gel Method

作　　者：乔健[1] 刘和义[1] 崔宏亮[1] 朱玉龙[1] 

机构地区：[1]南京理工大学材料科学与工程学院,南京210094

出　　处：《硅酸盐通报》2015年第1期260-264,共5页Bulletin of the Chinese Ceramic Society

基　　金：江苏省自然科学基金(BK2009390)

摘　　要：以无水氯化铝、铝粉、正硅酸乙酯(TEOS)为原料,通过溶胶-凝胶法合成了双相莫来石溶胶,采用离心纺丝法制备了多晶莫来石连续纤维。结果表明,前驱体溶胶具有良好的纺丝性和稳定性。凝胶纤维1100℃热处理2h,由无定型态转变成γ-Al2O3相,1300℃纤维莫来石化。1400℃烧结后,纤维表面光滑、直径均匀。随着热处理温度的提高,晶粒逐渐长大。Polycrystalline mullite continuous fibers were synthesized via a sol-gel centrifugal spinning technique. The diphasic mullite precursor was fabricated by using anhydrous aluminum chloride,aluminum powder and tetraethylorthosilicate（ TEOS） as starting materials. The result shows that,the precursor sol has an excellent spinnability and stability. When the gel fibers are sintered at 1100 ℃ for 2h,It turns from amorphous phase to γ-alumina and transforms to phase mullite at 1300 ℃. The fibers have a smooth surface and uniform diameter after fired at 1400 ℃. As the temperature increases,the grains gradually grow up.

关 键 词：莫来石纤维 溶胶-凝胶法 热处理制度 微观形貌 

分 类 号：TQ343[化学工程—化纤工业]