喷涂功率对等离子喷涂Al_2O_3-13%TiO_2涂层的影响研究  

The Study on Al_2O_3-13%TiO_2 Coating Prepared by Plasma Spraying at Different Powers

作　　者：张志刚[1] 缪强[1] 梁文萍[1] 崔世宇 徐一[1] 

机构地区：[1]南京航空航天大学,江苏南京210016

出　　处：《热处理》2015年第1期15-19,共5页Heat Treatment

基　　金：国家自然科学基金(51174119);航空科学基金(2012ZF52071)

摘　　要：采用等离子热喷涂技术以3种工艺参数在Q235钢基体上制备了Al2O3-13%Ti O2涂层。分别采用X射线衍射仪(XRD)、超三维景深设备(VHX-1000)、扫描电镜(SEM)和Image-Pro Plus软件对以不同功率获得的涂层的相组成、表面微观形貌、组织结构和孔隙率进行了分析。结果表明,随着喷涂功率的增大,涂层中α-Al2O3相向γ-Al2O3相的转变逐渐增多。此外,涂层的孔隙率由1.6%降低到0.38%;涂层表面微裂纹有减少的趋势。Al2 O3-13%TiO2 ceramic coating was prepared on Q235 steel by plasma spraying technology at three types of process parameters.The phase constituent,surface morphology,microstructure and porosity of the Al2 O3-13%TiO2 coating were investigated by XRD,VHX-1000 super depth-of-field 3D system,SEMand Image-Pro Plus software.The results show that more α-Al2 O3 phase will transform to γ-Al2 O3 phase with the increase of spraying power.In addition,the porosity reduced from 1 .6%to 0.38%,and the surface microcracks tended to decrease as the spraying power becomes greater.

关 键 词：喷涂功率 Al2 O3-13%TiO2 等离子喷涂 显微组织 孔隙率 

分 类 号：TG174.44[金属学及工艺—金属表面处理]