利用水淬锰渣制备B06级加气混凝土  

Preparation for B06 aerated concrete with using water quenching manganese slag

作　　者：陈平[1,2] 姜晗[1] 刘荣进[1,2] 

机构地区：[1]桂林理工大学材料科学与工程学院,广西桂林541004 [2]有色金属及材料加工新技术教育部重点实验室,广西桂林541004

出　　处：《混凝土》2015年第2期142-145,共4页Concrete

基　　金：广西科技攻关项目(桂科攻12118041-3D)

摘　　要：采用正交试验法对水淬锰渣制备加气混凝土配合比进行了研究,探讨了水泥掺量、石膏掺量、水淬锰渣掺量、石灰掺量和水料比5因素对加气混凝土制品干密度和抗压强度的影响,综合各因素后,得出制备B06级加气混凝土的适宜配合比,并通过SEM照片对试样微观结构进行了分析。Orthogonal experiment method is applied to research on mixture ratio design of aerated concrete with water quenching man- ganese slag, the effect of the content of cement, gypsum, water quenching manganese slag, lime and water - solid ratio on the density and strength of aerated concrete was investigated ,the comprehensive examination of each factor to the influence of five indexes, it was concluded that the suitable mix proportion of B06 aerated concrete, and the microstructure of the specimens was analysis through SEM photographs.

关 键 词：水淬锰渣 加气混凝土 抗压强度 

分 类 号：TU528.2[建筑科学—建筑技术科学]