聚乳酸/纳米SiO_2复合纤维的制备及力学性能  

Preparation and Mechanical Property of PLA/SiO_2 Composite Fibers

作　　者：刘盟盟[1] 蔡以兵[1,2] 靳子昂 魏取福[1] 刘伟 刘庆年 

机构地区：[1]江南大学生态纺织教育部重点实验室,无锡214122 [2]江苏箭鹿毛纺股份有限公司,宿迁223800

出　　处：《材料导报》2015年第2期96-100,共5页Materials Reports

基　　金：中国博士后科学研究基金(2014M560391);国家自然科学基金(51006046);国家863高技术研究发展计划项目(2012AA030313)

摘　　要：首先用硅烷偶联剂(GPS)对纳米SiO2进行接枝改性,利用粒径分析仪、FTIR和沉降实验对改性前后纳米SiO2的粒径大小、结构和溶剂稳定性的变化进行了表征;然后将改性前后的纳米SiO2分别与聚乳酸(PLA)在双螺杆挤出机中熔融混合,利用牵伸卷绕装置制备了PLA/SiO2和PLA/M-SiO2(改性后SiO2)复合纤维。利用视频显微镜和单纱强力仪研究了不同纳米SiO2含量对PLA/SiO2和PLA/M-SiO2复合纤维结构形貌和力学性能的影响,以及不同牵伸倍数对PLA/M-SiO2复合纤维结构形貌和力学性能的影响。结果表明M-SiO2粒径明显减小,且硅烷偶联剂结构中的有机官能团与SiO2表面硅羟基发生反应,减少了其表面Si-OH的量,使得M-SiO2表现出良好的溶剂稳定性和分散性;PLA/M-SiO2复合纤维的力学性能较PLA/SiO2复合纤维得到了明显的改善;当改性纳米SiO2含量为1%时复合纤维强度最好;当牵伸倍数为3时复合纤维强度最好。The modified nano-SiO2（M-SiO2）was prepared using silane coupling agent to graft and modify nanoSiO2.The particle size,structure and solvent stability of nano-SiO2 before and after modification were characterized by particle size analyzer,FTIR and settlement experiment,respectively.Then the PLA/SiO2 and PLA/M-SiO2 composite fibers were prepared using twin-screw extruder with molten mixing and followed by a draft collecting process.The effects of different SiO2 amounts on structural morphologies and mechanical properties of PLA/SiO2 and PLA/M-SiO2 composite fibers,and different drafting ratios on structural morphologies and mechanical properties of PLA/M-SiO2 composite fibers were studied by optical microscopy and signal-yarn strength tester.The results indicate that the organic modification decrease the particle size of nano SiO2.The M-SiO2 possesses excellent solvent stability and dispersion,attributed to the chemical reaction between organic functional groups of silane coupling agent and hydroxyl groups of nano silica surface.Compared to the PLA/SiO2 composite fibers,the mechanical properties of PLA/M-SiO2 composite fibers have notable improvements.The PLA/M-SiO2 composite fibers reach the maximum strength of the fiber,when the M-SiO2 amount and drafting ratio is 1% and 3times,respectively.

关 键 词：纳米SIO2 硅烷偶联剂改性 聚乳酸 复合纤维 力学性能 

分 类 号：TB332[一般工业技术—材料科学与工程]