Microstructures and mechanical properties of Mg-Al-Sm series heat-resistant magnesium alloys  

Mg-Al-Sm系耐热镁合金的显微组织和力学性能(英文)

作　　者：黄正华[1] 戚文军[1] 徐静[1] 蔡畅[1] 

机构地区：[1]广州有色金属研究院,广州510650

出　　处：《Transactions of Nonferrous Metals Society of China》2015年第1期22-29,共8页中国有色金属学报（英文版）

基　　金：Project(2013AA031001)supported by the National High-tech Research and Development Program of China;Project(2011A080403008)supported by the Major Science and Technology Project of Guangdong Province,China

摘　　要：The microstructures and phase compositions of the as-cast and die-cast Mg-6.02Al-1.03 Sm, Mg-6.05Al-0.98Sm-0.56 Bi and Mg-5.95Al-1.01Sm-0.57 Zn alloys were investigated. Meanwhile, the tensile mechanical and flow properties were tested. The results show that the as-cast microstructure of Mg-6.02Al-1.03 Sm alloy is composed of δ-Mg matrix, discontinuous δ-Mg17Al12 phase and small block Al2 Sm phase with high thermal stability. Rod Mg3Bi2 phase precipitates when Bi is added, while the added metal Zn dissolves into δ-Mg matrix and δ-Mg17Al12 phase. The as-cast alloys exhibit the excellent tensile mechanical property. The tensile strength（δb） and elongation（δ） can reach 205-235 MPa and 8.5%-16.0% at ambient temperature, respectively. Meanwhile, they can also exceed 160 MPa and 14.0% at 423 K, respectively. The die-cast microstructures are refined obviously, and meanwhile the broken second phases distribute dispersedly. The die-cast alloys exhibit better tensile mechanical properties with the values of δb and δ of 240-285 MPa and 8.5%-16.5% at ambient temperature, respectively, and excellent flow property with the flow length of 1870-2420 mm. The die-cast tensile fractures at ambient temperature exhibit a typical character of ductile fracture.分析铸态和压铸态Mg-6.02Al-1.03Sm、Mg-6.05Al-0.98Sm-0.56Bi和Mg-5.95Al-1.01Sm-0.57Zn合金的显微组织和相组成,测试其拉伸力学性能与流动性能。结果表明,Mg-6.02Al-1.03Sm合金铸态组织由δ-Mg基体、半连续的δ-Mg17Al12相和高热稳定性的小块状Al2Sm相组成。添加Bi后生成杆状Mg3Bi2相,而添加的Zn固溶于δ-Mg基体和δ-Mg17Al12相中。铸态合金呈现优异的拉伸力学性能,室温时其抗拉强度（δb）和伸长率（δ）分别达到205~235 MPa和8.5%~16.0%,而423 K时分别超过160 MPa和14.0%。压铸态组织明显细化,第二相发生破碎,且弥散分布。压铸态合金呈现更高的拉伸力学性能和优异的流动性能,室温δb和δ分别达到240~285 MPa和8.5%~16.5%,流动长度可达1870~2420 mm。压铸态室温拉伸断口呈现明显的断裂特征。

关 键 词：heat-resistant magnesium alloy Mg-Al-Sm alloy MICROSTRUCTURE mechanical property flow property fracture morphology 

分 类 号：TG146.22[一般工业技术—材料科学与工程]