Ar（12+）Induced Irradiation Damage in Bulk Metallic Glass(Cu47Zr45Al8)98.5Y1.5  

作　　者：张小楠 梅显秀 马雪 王英敏 羌建兵 王友年 

机构地区：[1]Key Laboratory of Materials Modification by Laser,Ion and Electron Beams,Dalian University of Technology

出　　处：《Chinese Physics Letters》2015年第2期110-114,共5页中国物理快报（英文版）

基　　金：Supported by the National Natural Science Foundation of China under Grant Nos 11079012 and 11375037;the National Basic Research Program of China under Grant No 2010CB832901

摘　　要：The highly charged ion Ar^12＋ with an energy of 3 Me V is used for irradiating metallic glass （Cu47Zr45Al8）98.5Y1.5 and polycrystalline metallic W at the irradiation fluences of 1× 10^14 ions/cm2, 1 × 10^15 ions/cm^2 and 1 × 10^16 ions/cm^2. The main structure of metallic glass remains an amorphous phase under different irradiation fluences according to x-ray diffraction analysis. The scanning electron microscope observation on the morphologies indicates that no significant irradiation damage occurs on the surface and cross section of the metallic glass sample after different fluences of irradiation, while a large area of irregular cracks and holes were observed on the surface of metallic W at a fluence of 1 ×10^16 ions/cm^2, with cracks and channel impairments at a certain depth from the surface. The root-mean-square （rms） roughness of metallic glass increases with increasing fluence of Ar^12＋, while the reflectance decreases with increasing irradiation fluence. A nano-hardness test shows that the hardness of metallic glass decreases after irradiation. Under certain a higher capability of resistance to Ar^12＋ irradiation in conditions, metallic glass （Cu47 Zr45Al8 ）98.5 Y1.5 exhibits comparison with polycrystalline W.The highly charged ion Ar^12＋ with an energy of 3 Me V is used for irradiating metallic glass （Cu47Zr45Al8）98.5Y1.5 and polycrystalline metallic W at the irradiation fluences of 1× 10^14 ions/cm2, 1 × 10^15 ions/cm^2 and 1 × 10^16 ions/cm^2. The main structure of metallic glass remains an amorphous phase under different irradiation fluences according to x-ray diffraction analysis. The scanning electron microscope observation on the morphologies indicates that no significant irradiation damage occurs on the surface and cross section of the metallic glass sample after different fluences of irradiation, while a large area of irregular cracks and holes were observed on the surface of metallic W at a fluence of 1 ×10^16 ions/cm^2, with cracks and channel impairments at a certain depth from the surface. The root-mean-square （rms） roughness of metallic glass increases with increasing fluence of Ar^12＋, while the reflectance decreases with increasing irradiation fluence. A nano-hardness test shows that the hardness of metallic glass decreases after irradiation. Under certain a higher capability of resistance to Ar^12＋ irradiation in conditions, metallic glass （Cu47 Zr45Al8 ）98.5 Y1.5 exhibits comparison with polycrystalline W.

关 键 词：ZR Induced Irradiation Damage in Bulk Metallic Glass AR CU 

分 类 号：TG139.8[一般工业技术—材料科学与工程]