Microstructure and Mechanical Properties of Precipitation Strengthened Fire Resistant Steel Containing High Nb and Low Mo  

作　　者：Zheng-yan ZHANG Qi-long YONG Xin-jun SUN Zhao-dong LI Jun-yu KANG Guo-dong WANG 

机构地区：[1]Department of Structural Steels,Central Iron and Steel Research Institute [2]State Key Laboratory of Rolling and Automation,Northeastern University

出　　处：《Journal of Iron and Steel Research International》2015年第4期337-343,共7页

基　　金：Item Sponsored by National Basic Research Program of China(2010CB630805)

摘　　要：Through the thermo-mechanical control process （TMCP）, a high Nb low Mo fire resistant steel with the yield strength （YS） of 521 MPa at room temperature （RT） and 360 MPa at elevated temperature （ET） of 600 ℃ was developed based on MX （M=Nb, V, Mo; X=C,N） precipitation strengthening. A series of tensile and con- stant load tests were conducted to study the mechanical properties at ET. The dynamic continuous cooling transfor- mation （CCT） as well as precipitation behavior of microalloy carbonitride was investigated by means of thermal sim- ulator and electron microscopy approaches. Results showed that the failure temperature of tested steel was deter- mined as 653 ℃, and the granular bainite was obtained when the cooling rate was higher than 10 ℃/s. In the rolled state, a certain amount of M/A islands was observed. During heating from RT to ET, M/A islands disappeared, and cementites and high dense compound precipitates （Nb, Mo, V）C with size of less than 10 nm precipitated in ferrite at ET （600 ℃）, which resulted in precipitation strengthening at ET.Through the thermo-mechanical control process （TMCP）, a high Nb low Mo fire resistant steel with the yield strength （YS） of 521 MPa at room temperature （RT） and 360 MPa at elevated temperature （ET） of 600 ℃ was developed based on MX （M=Nb, V, Mo; X=C,N） precipitation strengthening. A series of tensile and con- stant load tests were conducted to study the mechanical properties at ET. The dynamic continuous cooling transfor- mation （CCT） as well as precipitation behavior of microalloy carbonitride was investigated by means of thermal sim- ulator and electron microscopy approaches. Results showed that the failure temperature of tested steel was deter- mined as 653 ℃, and the granular bainite was obtained when the cooling rate was higher than 10 ℃/s. In the rolled state, a certain amount of M/A islands was observed. During heating from RT to ET, M/A islands disappeared, and cementites and high dense compound precipitates （Nb, Mo, V）C with size of less than 10 nm precipitated in ferrite at ET （600 ℃）, which resulted in precipitation strengthening at ET.

关 键 词：fire resistant steel elevated temperature property MICROALLOYING granular bainite precipitation strengthening 

分 类 号：TG142.1[一般工业技术—材料科学与工程]