6061-T6铝合金超声振动强化搅拌摩擦焊接头组织与性能  

Microstructure and properties of 6061-T6 Al alloy joint by ultrasonic enhanced friction stir welding

作　　者：孟强[1] 王怡嵩[1] 刘小超[2] 高嵩[2] 武传松[2] 

机构地区：[1]北京赛福斯特技术有限公司,101107 [2]山东大学材料连接技术研究所,济南市250061

出　　处：《焊接》2015年第4期49-53,75,共5页Welding & Joining

摘　　要：将超声振动施加在搅拌头前方的待焊工件上,开展了6061-T6铝合金板超声振动强化搅拌摩擦焊工艺试验。通过显微组织观察、拉伸试验和显微硬度测试来评价接头组织与性能,比较了超声振动条件下的接头组织与性能与常规搅拌摩擦焊接头的差异。试验结果表明,超声振动细化了焊核区和热机影响区的晶粒组织,提高了接头抗拉强度、断后伸长率和显微硬度。Ultrasonic vibration was exerted on workpiece at the front of the stir pin,and ultrasonic enhanced friction stir welding(UeFSW) experiments of 6061-T6 Al alloy were carried out.By analyzing microstructure,testing the tensile strength and microhardness,the microstructure and properties of joint by UeFSW were compared with that of the traditional FSW.The results show that ultrasonic vibration can make the microstructuies of nugget zone and thermal-mechanical affected zone be finer,increase the tensile strength,elongation and microhardness of the joint.

关 键 词：6061-T6铝合金 搅拌摩擦焊 超声振动 显微组织 力学性能 

分 类 号：TG456[金属学及工艺—焊接]