Stability of BN/metal interfaces in gaseous atmosphere  

作　　者：Yang Yang Qiang Fu Mingming Wei Hendrik Bluhm Xinhe Bao 

机构地区：[1]State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, China [2]Chemical Sciences Division, Lawrence Berkeley National Laboratory, 1 Cyclotron Road, Berkeley, California 94720, USA

出　　处：《Nano Research》2015年第1期227-237,共11页纳米研究（英文版）

摘　　要：Hexagonal boron nitride （h-BN） is often prepared by epitaxial growth on metals, and stability of the formed BN/metal interfaces in gaseous environment is a key issue for physicochemical properties of the BN overlayers. As an illustration here, the structural change of a BN/Ru（0001） interface upon exposure to 02 has been investigated using in situ photoemission electron microscopy （PEEM） and ambient pressure X-ray photoelectron spectroscopy （AP-XPS）. We demonstrate the occurrence of oxygen intercalation of the BN overlayers in 02 atmosphere, which decouples the BN overlayer from the substrate. Comparative studies of oxygen intercalation at BN/Ru（0001） and graphene/Ru（0001） surfaces indicate that the oxygen intercalation of BN overlayers happens more easily than graphene. This finding will be of importance for future applications of BN-based devices and materials under ambient conditions.六角形的硼氮化物(h-BN ) 被取向附生的生长经常在气体的环境在形成的 BN/metal 接口的金属，和稳定性上准备是为 BN overlayers 的物理化学的性质的一个关键问题。作为这里的一幅插图，在到 O 的暴露之上的一个 BN/Ru (0001 ) 接口的结构的变化 < 潜水艇 class= “ a-plus-plus ” > 2 </sub> 被调查了在 situ 光致核裂变电子显微镜学(PEEM ) 和周围的压力 X 光检查光电子光谱学(AP-XPS ) 使用。我们在 O 表明 BN overlayers 的氧置闰的出现 < 潜水艇 class= “ a-plus-plus ” > 2 </sub> 空气，哪个 decouples 从底层的 BN overlayer。在 BN/Ru (0001 ) 和 graphene/Ru (0001 ) 的氧置闰的比较研究表面显示 BN overlayers 的氧置闰比 graphene 更容易发生。这发现将在周围的条件下面具有为基于 BN 的设备和材料的未来应用的重要性。

关 键 词：H-BN graphene INTERCALATION Ru（0001） PEEM AP-XPS 

分 类 号：TQ175.14[化学工程—硅酸盐工业] TQ464.1