CO_2与环氧丙烷合成碳酸丙烯酯的多相催化剂研究  

Synthesis of propylene carbonate from CO_2 and propylene oxide over a novel heterogeneous catalyst

作　　者：张建[1,2] 张志智[2,3] 孙潇磊[2] 孙万付[2] 方向晨[2,3] 

机构地区：[1]辽宁石油化工大学,辽宁抚顺113001 [2]抚顺石油化工研究院,辽宁抚顺113001 [3]华东理工大学,上海112004

出　　处：《天然气化工—C1化学与化工》2015年第3期41-44,共4页Natural Gas Chemical Industry

基　　金：中国石化股份有限公司资助(项目编号:061301)

摘　　要：通过混合氯球固载化的离子液体(PS-Mim)、助剂A和助剂B,然后压制成型,制备了一种新型的多相固体催化剂(PS-Mim-A-B),并在固定床反应器上评价其由CO2和环氧丙烷(PO)合成碳酸丙烯酯(PC)的催化性能。考察了温度、压力、空速、反应物的比例对反应的影响。结果表明,该催化剂具有极高的催化活性。当反应温度为120℃、压力为2MPa、空速为1h-1、CO2和PO进料物质的量比为2∶1时,PC的收率可达96%以上,PC的选择性在99.5%左右。A novel heterogeneous catalyst PS-Mim-A-B was prepared by mixing the chloromethylated bead supported ionic liquid PS-Mim with the promoters A and B then pressing into tablets, and its catalytic performance for synthesis of propylene carbonate （PC） from CO2 and propylene oxide （PO） was evaluated in a fixed bed reactor. The effects of reaction temperature, pressure, LHSV and CO2/PO mole ratio on the reaction were investigated. Results showed that the catalyst had excellent catalytic activity. Under the optimum reaction conditions of 120℃, 2MPa, LSHV of 1h-1 and CO2/PO mole ratio of 2：1, PC yield could be over 96%with a selectivity of about 99.5%.

关 键 词：二氧化碳 环氧丙烷 碳酸丙烯酯 合成 固定床 多相催化剂 

分 类 号：TQ225.24[化学工程—有机化工] O643[理学—物理化学]