Al^(3+)离子介入提升(NH_4)_2SiF_6对SBA-15介孔材料的水热稳定化作用（英文）  

Incorporation of Al^(3+) ions to promote the stabilization effect of (NH_4)_2SiF_6 treatment on the hydrothermal stability of mesoporous SBA-15 zeolite

作　　者：邹成龙[1] 沙观宇 黄曜[2] 牛国兴[1] 赵东元[1] 

机构地区：[1]复旦大学化学系,上海200433 [2]复旦大学材料系,上海200433

出　　处：《催化学报》2015年第7期1001-1008,共8页

基　　金：financially supported by the National Basic Research Program of China(973 Program,2010CB226901,2013CB934100);the National Natural Science Foundation of China(U1463206)~~

摘　　要：提出了一种(NH4)2Si F6处理提高SBA-15介孔材料水热稳定性的改良方法.采用SBA-15介孔材料中预引入Al3+离子,再进行1%SiO 2计量的(NH4)2Si F6处理,最后用强酸洗脱预引入的Al3+.结果显示,由此处理的SBA-15材料,其水热稳定性明显优于相同条件下未预引入Al3+时(NH4)2Si F6处理的样品.两者在800°C、100%水蒸气处理12 h后,虽然均能很好保持其介观有序度、形貌及六方孔道结构,但前者的比表面积可高达271 m2/g,而后者仅为224 m2/g.表明Al3+离子介入能大幅度提升(NH4)2Si F6处理对SBA-15介孔材料的稳定化作用.这主要得益于预引入的骨架Al3+在保障(NH4)2Si F6处理修复SBA-15材料表面缺陷和进行表面疏水化、提升其水热稳定性的同时,能减缓(NH4)2Si F6释放的多余F离子对SBA-15材料骨架的刻蚀破坏作用.Al3+离子介入的这种提升作用与其引入方式和SBA-15材料所经受的温度密切相关.This work demonstrates an improved（NH4）2SiF 6 treatment to enhance the hydrothermal stability of mesoporous SBA-15 zeolite. In this treatment, Al3＋ ions are incorporated into SBA-15 zeolite first, then it is treated with 5%（NH4）2SiF 6 solution according to 1% SiO 2 of SBA-15 and finally washed with HCl（2 mol/L） to remove the pre-incorporated Al3＋ ions. The obtained SBA-15 exhibits higher hydrothermal stability than that without pre-incorporated Al3＋. Compared with the latter, the sample maintains a better ordered mesostructure and a larger surface area（271 m2/g） after hydrothermal treatment at 800 °C for 12 h in 100% steam. The results show that incorporating Al3＋ ions into SBA-15 zeolite before（NH4）2SiF 6 treatment obviously promotes the stabilization effect of（NH4）2SiF 6 treatment. The mechanism suggests that the incorporated Al3＋ ions can effectively capture F- ions that have been released from（NH4）2SiF 6, and thus reduce their etching into the SBA-15 zeolite framework. This ensures that the positive factors of（NH4）2SiF 6 treatment, such as silicon insertion and surface hydrophobization by F- ions, play effective roles in the improvement of the hydrothermal stability of SBA-15 zeolite. This promoting effect of the Al3＋ ions is closely related to the method that is used to introduce the Al3＋ and the SBA-15 zeolite processing temperature.

关 键 词：SBA-15沸石介孔材料 水热稳定性 氟硅酸铵 Al3+离子引入 补硅 