TC4/TA18钛合金蜂窝夹层结构钎焊工艺研究  

Brazing Process of TC4/TA18 Titanium Alloy Honeycomb Sandwich Construction

作　　者：高兴强[1] 佀好学[1] 岳喜山[1] 静永娟[1] 李智渊[1] 

机构地区：[1]中航工业北京航空制造工程研究所航空焊接与连接技术航空科技重点实验室

出　　处：《航空制造技术》2015年第11期109-111,116,共4页Aeronautical Manufacturing Technology

摘　　要：针对TC4/TA18钛合金蜂窝夹层结构,采用Ti-37.5Zr-15Cu-10Ni非晶箔带钎料,研究钎焊温度和保温时间对TC4/TA18钛合金蜂窝夹层结构接头微观组织及力学性能的影响,优化出TC4/TA18钛合金蜂窝夹层结构较优的钎焊工艺为920℃/保温90min和钎料添加量80μm,该工艺参数下钎焊接头的室温拉脱强度平均值最高,可达19.82MPa,破坏部位为TA18钛合金蜂窝芯。TC4/TA18 titanium alloy honey-comb sandwich construction is brazed by amorphous foil solder Ti-37.5Zr-15Cu-15Ni （mass fraction）. The effect of brazing temperature and holding time on the micro-structure of brazing interface and the tensile strength of TC4/TA18 titanium alloy honeycomb sandwich construc-tion is researched. The optimized brazing technology is 920℃/90min with 80μm solder in depth. With the opti-mized brazing technology, the average value of the tensile strength of specimens is 19.82MPa, and the honeycomb core is the weak part.

关 键 词：TA18钛合金 蜂窝夹层结构 钎焊 