助交联剂TMPTMA在高硬度丁腈胶料中的应用  

Application of Cross-linking Agent TMPTMA in NBR Compounds with High Hardness

作　　者：王诗凝[1] 冯芝娟[1] 程超[1] 肖建斌[1] 

机构地区：[1]青岛科技大学橡塑材料与工程教育部重点实验室,山东青岛266042

出　　处：《青岛科技大学学报（自然科学版）》2015年第3期308-310,共3页Journal of Qingdao University of Science and Technology:Natural Science Edition

摘　　要：研究助交联剂TMPTMA(三羟甲基丙烷三甲基丙烯酸酯)用量对NBR(丁腈)混炼胶加工性能和硫化胶力学性能的影响。结果表明:助交联剂TMPTMA不仅有加快硫化速率的作用,也具有一定的增塑效果,使混炼胶的流动性提高,同时明显提高胶料的交联密度;随着TMPTMA用量的增加,NBR硫化胶的硬度、拉伸强度、撕裂强度、100%定伸应力增大,而拉断伸长率和回弹性减小;压缩永久变形有所降低,共混胶的磨耗体积先减小后增大。The effects of different quantity of cross-linking agent TMPTMA on the prop- erties of NBR compounds were studied. The results showed that the cross-linking agent TMPTMA not only accelerated the curing rate but also had a certain plasticizing effect and improved the processing performance of the blends, at the same time greatly im- proved the density of cross linking. With the content of TMPTMA increasing, the ten- sile strength, tear strength, modulus at 100% and hardness of NBR compounds in- creased, but the elongation at break, the compression permanent set and resilenee re- duced. With the content of TMPTMA increasing, the abrasion quantity of NBR com- pounds first deereased and then increased.

关 键 词：TMPTMA 丁腈橡胶 交联密度 硬度 

分 类 号：TQ333.7[化学工程—橡胶工业]