钢绞线用钢的LF脱硫生产实践  

PRODUCTION PRACTICE ON LF DESULPHURIZATION TECHNOLOGY OF STEEL USED FOR STEEL STRAND

作　　者：张新建[1] 张毅[1] 

机构地区：[1]首钢水城钢铁集团有限责任公司,贵州六盘水553028

出　　处：《冶金信息导刊》2015年第3期34-36,51,共4页Metallurgical Information Review

摘　　要：水钢生产钢绞线用钢的铁水未进行预脱硫处理，LF脱硫负荷较重，通过分析LF炉精炼渣的组成对其脱硫能力、化学反应速度等性能的影响，确定了精炼渣的基本组成为CaO-SiO2-MgO—Al2O3渣系及其含量。在生产中，通过改进转炉挡渣、优化炉渣脱氧及吹氩、温度控制，使LF精炼脱硫率达到70％，产品中硫含量控制在0．007％的水平，保障了产品质量。Since the hot metal used for producing strand steel was not pre-desulfurized, desulfurization load of LF was heavy. By analyzing the influences of LF refining slag composition on its desulfurization ability, chemical reaction rate and so on, CaO-SiO2-MgO-Al2O3 refining slag is chose and its composition is defined. By improving converter blocking slag and optimizing deoxidization of slag, argon-blowing technology and temperature control, desulfurization rate of LF refining process has reached 70% and the average sulfur content in steel is the level of 0.007%, assuring the quality of steel products.

关 键 词：LF 精炼渣 脱硫率 分配比 

分 类 号：TF535.22[冶金工程—钢铁冶金]