掺杂型烧绿石La2Sn1.7Co0.3O7-δ逆负载CeO2催化剂的甲烷催化燃烧性能  

Inverse CeO_2/La_2Sn_(1. 7)Co_(0. 3)O_(7-δ) Catalyst for Methane Catalytic Combustion

作　　者：李伶聪 胡瑞生[1] 白雅琴[1,4] 李景佳 唐海莲[2] 王军虎[2] 季生福[3] 

机构地区：[1]内蒙古大学化学化工学院、稀土材料化学与物理重点实验室,呼和浩特010021 [2]中国科学院大连化学物理研究所,大连116011 [3]北京化工大学,化工资源有效利用国家重点实验室,北京100029 [4]呼和浩特职业学院化学系

出　　处：《高等学校化学学报》2015年第7期1328-1336,共9页Chemical Journal of Chinese Universities

基　　金：国家自然科学基金(批准号:21263008);北京化工大学化工资源有效利用国家重点实验室开放课题(批准号:CRE-2014-C-304)资助~~

摘　　要：用溶胶凝胶-浸渍法在900℃煅烧3 h后制备了烧绿石逆负载型催化剂Ce O2/La2Sn1.7Co0.3O7-δ,并用于甲烷催化燃烧反应,显示出较好的催化燃烧活性.催化剂还具有良好的高温热稳定性和可重复利用性能,可使甲烷转化90%的温度(T90)降到564℃,与相同条件下制备的单一烧绿石型催化剂La2Sn1.7Co0.3O7-δ和La2Sn1.7Co0.3O7-δ与Ce O2机械混合的催化剂相比,T90分别降低78和135℃.X射线衍射结果表明,烧绿石型逆负载催化剂具有Ce O2和La2Sn1.7Co0.3O7-δ2种物相,在逆负载型催化剂中的Ce O2比机械混合催化剂中的Ce O2分散程度更好;H2程序升温还原实验也证实逆负载催化剂Ce O2/La2Sn1.7Co0.3O7-δ的相应3个还原峰温度均比单一烧绿石型催化剂La2Sn1.7Co0.3O7-δ相应3个还原峰温度明显降低;透射电子显微镜和原子力显微镜结果表明,逆负载催化剂Ce O2/La2Sn1.7Co0.3O7-δ抗烧结能力强,颗粒分散均匀,粒径尺寸相应较小;穆斯堡尔谱和X射线光电子能谱结果证明逆负载催化剂Ce O2/La2Sn1.7Co0.3O7-δ结构中结晶相Sn4+含量较高,表面晶格氧数量较多,这是烧绿石逆负载型催化剂具有良好甲烷催化燃烧性质的主要原因.The inverse CeO2/La2 Sn1.7 CO0. 3 O7-δcatalyst was prepared by sol-gel and impregnation method calcined at 900 ℃ and investigated in the methane catalytic combustion. The catalytic activity evaluated for methane combustion showed that the methane conversion temperature of Tgo was 564 ℃ , compared with the pure La2Sn0. 7 Co0. 3 O7-δ prepared in the same condition and mechanical mixing of La2 Sn1. 7 Co0. 3 O7-δ and CeO2, T90 decreased by 78 ℃ and 135 ℃, respectively, and the inverse CeO2/La2Sn1.7CO0.3O7-δ catalyst not only had the excellent methane combustion activity, but also had the well thermal stability and reusable performance. The excellent performance of the inverse CeOE/LaESnl. 7 Co0. 3O7-δcatalyst was represented by the characterizations of XRD, TEM, AFM, TPR, BET, XPS and Mtissbauer spectra. XRD characterization showed that the inverse CeOE/La2 Sn1. 7 Co0. 3 O7-δ catalyst not only had the La2 SnL 7 CO0. 3 O7-δ structure, but also had the CeO2 phase, and the CeO2 had been well disperse on the La2 Sn1.7 Co0.3 O7-δcomposite oxide; TPR indicated that the CeO2/La2Sn1.7 Co0.3 O7-δ had lower reduction temperature compared to La2Sn1.7 Co0.3O7-δ, XPS and Mossbauer spectra indicated that the Sn4＋ is the main valence state in the inverse catalyst, and the lattice oxygen play an important role in catalytic activity; TEM and BET tests showed that the CeO2/ La2Sn1.7Co0.307-δ particles had better dispersed and larger surface area than La2Sn1.7Co0.3 07-δ. All above explained the reasons of the CeOE/La2 Sn1.7 Co0.3 07-δ catalyst had excellent catalytic activity toward methane combustion.

关 键 词：逆负载催化剂 烧绿石 二氧化铈 甲烷催化燃烧 

分 类 号：O643.36[理学—物理化学]