Nickel-coated Steel Stud to Aluminum Alloy Joints Made by High Frequency Induction Brazing  

作　　者：葛佳棋 王克鸿 ZHANG Deku WANG Jian 

机构地区：[1]School of Material Science and Engineering, Nanjing University of Science and Technology

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2015年第3期601-606,共6页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Defense Basic Research Program(No.A2620110005);the Equipment Pre Research Project of Eleventh Five-Year Plan of China(No.40401050301);the Natural Science Foundation of Jiangsu Province(No.BK20131261)

摘　　要：Nickel-coated 45 steel studs and 6061 aluminum alloy with 4047 A1 alloy foil as filler metal were joined by using high frequency induction brazing. The microstrueture of Fe/A1 brazed joint was studied by means of optical microscopy （OM）, scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, and X-ray diffraction （XRD）. Results showed that 45 steel stud and 6061 aluminum alloy could be successfully joined by high frequency induction brazing with proper processing parameters. The bonding strength of the joint was of the order of 88 MPa. Ni coating on steel stud successfully avoided the generation of Fe-AI intermetallic compound which is brittle by blocking the contact between A1 and Fe. Intermetallic compounds, i e, AI3Ni2, AlmNi0.9 and A10.3Fe3Si0.7 presented in AI side, FeNi and Fe-A1-Ni ternary eutectic structure were formed in Fe side. The micro-hardness in intermetallic compound layer was 313 HV. The joint was brittle fractured in the intermetallic compounds layer of A1 side, where plenty of A13Ni2 intermetallie compounds were distributed continuously.Nickel-coated 45 steel studs and 6061 aluminum alloy with 4047 A1 alloy foil as filler metal were joined by using high frequency induction brazing. The microstrueture of Fe/A1 brazed joint was studied by means of optical microscopy （OM）, scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, and X-ray diffraction （XRD）. Results showed that 45 steel stud and 6061 aluminum alloy could be successfully joined by high frequency induction brazing with proper processing parameters. The bonding strength of the joint was of the order of 88 MPa. Ni coating on steel stud successfully avoided the generation of Fe-AI intermetallic compound which is brittle by blocking the contact between A1 and Fe. Intermetallic compounds, i e, AI3Ni2, AlmNi0.9 and A10.3Fe3Si0.7 presented in AI side, FeNi and Fe-A1-Ni ternary eutectic structure were formed in Fe side. The micro-hardness in intermetallic compound layer was 313 HV. The joint was brittle fractured in the intermetallic compounds layer of A1 side, where plenty of A13Ni2 intermetallie compounds were distributed continuously.

关 键 词：45 steel stud 6 061 aluminum alloy high frequency induction brazing dissimilar metaljoint mechanical property microstructure 

分 类 号：TG454[金属学及工艺—焊接]