作　　者：M.Ravichandran A.Naveen Sait V.Anandakrishnan 

机构地区：[1]Department of Mechanical Engineering, Chendhuran College of Engineering and Technology [2]Department of Production Engineering, National Institute of Technology

出　　处：《Rare Metals》2014年第6期686-696,共11页稀有金属（英文版）

摘　　要：The cold upsetting studies were carried out for the aluminium metal matrix hybrid composites in the present study. Aluminium metal matrix hybrid composites were synthesised through powder metallurgy route from ball-milled powders to yield the following compositions：Al ＋ 2.5 wt% TiO2＋ 2 wt% Gr, Al ＋ 2.5 wt% TiO2＋ 4 wt% Gr, Al ＋ 5.0 wt% TiO2＋ 2 wt% Gr and Al ＋ 5.0 wt% TiO2＋ 4 wt% Gr. The compaction process was carried out using suitable punch and die in 40 k N hydraulic press, and sintering was done in an electric muffle furnace at the temperature of 590 °C for 3 h. The sintered preforms were subjected to incremental compressive loading of 10 k N until the cracks were found at the free surface. The true axial stress, true hoop stress, true hydrostatic stress and true effective stress were calculated for all the preforms, and all these stresses are correlated with the true axial strain. The stress ratio parameters（rz/reff, rh/reff, rz/rmand rh/rm） of the all preforms were correlated with true axial strain. The maximum true axial stress, true hoop stress, true effective stress and hydrostatic static stress are obtained for the composite containing5 wt% of TiO2 and 4 wt% of graphite and the minimum ones are obtained for composite containing 2.5 wt% of TiO2 and 2 wt% of graphite.The cold upsetting studies were carried out for the aluminium metal matrix hybrid composites in the present study. Aluminium metal matrix hybrid composites were synthesised through powder metallurgy route from ball-milled powders to yield the following compositions：Al ＋ 2.5 wt% TiO2＋ 2 wt% Gr, Al ＋ 2.5 wt% TiO2＋ 4 wt% Gr, Al ＋ 5.0 wt% TiO2＋ 2 wt% Gr and Al ＋ 5.0 wt% TiO2＋ 4 wt% Gr. The compaction process was carried out using suitable punch and die in 40 k N hydraulic press, and sintering was done in an electric muffle furnace at the temperature of 590 °C for 3 h. The sintered preforms were subjected to incremental compressive loading of 10 k N until the cracks were found at the free surface. The true axial stress, true hoop stress, true hydrostatic stress and true effective stress were calculated for all the preforms, and all these stresses are correlated with the true axial strain. The stress ratio parameters（rz/reff, rh/reff, rz/rmand rh/rm） of the all preforms were correlated with true axial strain. The maximum true axial stress, true hoop stress, true effective stress and hydrostatic static stress are obtained for the composite containing5 wt% of TiO2 and 4 wt% of graphite and the minimum ones are obtained for composite containing 2.5 wt% of TiO2 and 2 wt% of graphite.

关 键 词：Metal matrix composites Cold upsetting Powder metallurgy 

分 类 号：TG316[金属学及工艺—金属压力加工] TF125[冶金工程—粉末冶金]