Influencing factor of sinter body strength and its effects on iron ore sintering indexes  

作　　者：Guo-liang Zhang Sheng-li Wu Bo Su Zhi-gang Que Chao-gang Hou Yao Jiang 

机构地区：[1]School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing

出　　处：《International Journal of Minerals,Metallurgy and Materials》2015年第6期553-561,共9页矿物冶金与材料学报（英文版）

基　　金：financially supported by the Fundamental Research Funds for the Central Universities of China (No. FRF-IC-14-006)

摘　　要：Sinter body strength, which reflects the strength of sinter, plays an important role in the improvement of sinter. In this study, the sinter body strengths of iron ores were measured using a microsintering method. The relationship between the chemical composition and sinter body strength was discussed. Moreover, sinter-pot tests were performed. The effects of sinter body strength on the sintering indexes were then elucidated, and the bottom limit of sinter body strength of blending ores was confirmed. In the results, the compressive strengths（CSs） of iron ores are observed to decrease with the increasing of the contents of loss on ignition（LOI）, SiO 2, and Al2O3; however, LOI of less than 3wt% does not substantially influence the CSs of fine ores. In the case of similar mineral composition, the porosity, in particular, the ratio between the number of large pores and the total number of pores, strongly influences the sinter body strength. With an increase of the blending-ore CSs used in sinter-pot tests, the yield, productivity, and tumbler strength increase, and the solid fuel consumption decreases. The CSs of the blending ores only slightly affect the sintering time. The CS bottom limit of the blending ores is 310 N. When the CSs of the blending ores increase by 10%, the yield, productivity, and tumbler index increase by 1.9%, 2.8%, and 2.0%, respectively, and the solid fuel consumption decreases by 1.9%.Sinter body strength, which reflects the strength of sinter, plays an important role in the improvement of sinter. In this study, the sinter body strengths of iron ores were measured using a microsintering method. The relationship between the chemical composition and sinter body strength was discussed. Moreover, sinter-pot tests were performed. The effects of sinter body strength on the sintering indexes were then elucidated, and the bottom limit of sinter body strength of blending ores was confirmed. In the results, the compressive strengths（CSs） of iron ores are observed to decrease with the increasing of the contents of loss on ignition（LOI）, SiO 2, and Al2O3; however, LOI of less than 3wt% does not substantially influence the CSs of fine ores. In the case of similar mineral composition, the porosity, in particular, the ratio between the number of large pores and the total number of pores, strongly influences the sinter body strength. With an increase of the blending-ore CSs used in sinter-pot tests, the yield, productivity, and tumbler strength increase, and the solid fuel consumption decreases. The CSs of the blending ores only slightly affect the sintering time. The CS bottom limit of the blending ores is 310 N. When the CSs of the blending ores increase by 10%, the yield, productivity, and tumbler index increase by 1.9%, 2.8%, and 2.0%, respectively, and the solid fuel consumption decreases by 1.9%.

关 键 词：iron ore sinter compressive strength influencing factors sintering 

分 类 号：TF046.4[冶金工程—冶金物理化学] TQ163[化学工程—高温制品工业]