航空透明聚氨酯胶片动态力学性能实验研究  

Experimental study on dynamic mechanical behavior of aerospacetransparent polyurethane interlayer

作　　者：姚小虎[1] 张龙辉[1] 张晓晴[1] 郭伟国[2] 臧曙光[3] 

机构地区：[1]华南理工大学土木与交通学院,广州510640 [2]西北工业大学航空学院,西安710072 [3]中国建筑材料检验认证中心有限公司,北京100024

出　　处：《航空学报》2015年第7期2236-2243,共8页Acta Aeronautica et Astronautica Sinica

基　　金：国家自然科学基金(11372113);国家国际科技合作项目(2011DFA53080);爆炸科学与技术国家重点实验室基金(KFJJ14-2M);亚热带建筑科学国家重点实验室自主研究课题(2014ZC18)~~

摘　　要：对夹层玻璃中聚氨酯胶片的动态力学性能进行系统研究,可以为飞机和高铁风挡玻璃抗冲击性能的设计提供可靠的材料数据和模型。利用温度控制的Hopkinson拉、压杆试验装置和微型材料试验机（MTS5587）对聚氨酯胶片在-40~50℃温度范围、0.001~6 500s^-1应变率范围内的力学行为进行了系统研究。结果表明：航空透明聚氨酯的力学性能具有明显的温度敏感性和应变率敏感性,随着应变率提高或温度降低,聚氨酯胶片的流动应力和割线模量也相应增加,表现出明显的应变率和温度效应,同时两者可能有一定的等效性。温度从-20℃下降到-40℃时,应力-应变曲线变化显著,表现出向玻璃态转变的特性。在0℃以上的温度时,同应变率下,动态拉伸应力-应变曲线的应力值要低于动态压缩曲线的应力值。而在温度低于0℃时,在同应变率下,动态拉伸应力-应变曲线的应力值则高于动态压缩曲线的应力值。Study on the dynamic properties of the polyurethane interlayer of laminated glass can provide material data and model for the impact resistance design of windshield of aircraft and high speed rail. The mechanical behavior of the polyurethane interlayer was investigated experimentally with the temperatures from - 40℃ to 50℃ and strain rates from 0. 001 s^-1 to 6 500 s^-1. Tests were performed by MTS5587 servo hydraulic testing machine and the split Hopkinson tension and com- pression bar, for low and high strain rate tests respectively. The obtained results show that the dynamic tensile response of the polyurethane interlayer is sensitive to temperature and strain rate. As strain rate increases and temperature decreases, flow stress goes up and hardening resistance behavior becomes more apparent. When the temperature decreases from - 20 10 to -- 40 10, the stress-strain curves change significantly, the specimen transmits from a rubbery behavior to a glassy behavior. When the temperature is above 0 ℃, at a certain strain rate, dynamic tensile stresses are lower than dynamic compressive stresses, but when the temperature is below 0 ℃, dynamic tensile stresses are higher than dynamic compressive stress at the same strain.

关 键 词：夹层风挡 透明聚氨酯胶片 HOPKINSON杆 温度效应 应变率效应 

分 类 号：TQ323.8[化学工程—合成树脂塑料工业]