氧化淀粉交联改性PVA胶粘剂的制备和性能研究  

Study on preparation and properties of PVA adhesive crosslinked and modified by oxidized starch

作　　者：王少会[1] 李春燕[1] 郭赞如[1] 章家立[1] 

机构地区：[1]华东交通大学理学院化学化工系,江西南昌330013

出　　处：《中国胶粘剂》2015年第7期1-4,9,共5页China Adhesives

基　　金：江西省教育厅自然科学基金项目(GJJ13323);国家自然科学基金项目(21164001)

摘　　要：以聚乙烯醇(PVA)和红薯淀粉为原料、硼砂为交联剂、双氧水(H2O2)和过硫酸铵(APS)为氧化剂,采用氧化交联法制备了环保、耐水和高强的氧化淀粉交联改性PVA胶粘剂。研究结果表明:淀粉和PVA之间发生了氧化反应,并形成了交联结构;当w(淀粉)=40%、w(H2O2)=3%、w(APS)=0.45%和w(硼砂)=2.0%(均相对于PVA质量而言)时,改性胶粘剂的综合性能相对最好,其胶接强度、耐水性分别为0.88 MPa、95 h,并且其流动性好、无霉变现象。With polyvinyl alcohol （PVA） and sweet potato starch as raw materials, borax as crosslinker, hydrogen peroxide（H2O2） anti ammonium persulfate（APS） as oxidants, an environment friendly PVA adhesive with water resistance and high strength, which was crosslinked and modified by oxidized starch, was prepared by oxidative crosslinking method. The research results showed that the crosslinking structure between starch and PVA was h）rmed by oxidation. The modified adhesive had the relatively best combination property because its bonding strength anti water resistance were 0.88 MPa and 95 h respectively, and it had the good liquidity and hadn＇ t mihtew phenomenon when mass fractions of starch, H202, APS and borax were 40%, 3%, 0.45% and 2.0% respectively in PVA.

关 键 词：胶粘剂 氧化淀粉 聚乙烯醇 交联 改性 

分 类 号：TQ432.2[化学工程] TQ433.439