间歇反应釜法石灰表面包覆实验研究  

Experimental Study on CaO Surface Coated by Batch Reactor

作　　者：亢淑梅[1] 沈明钢[1] 李维娟[1] 钱锦秀[1] 孙钰沣 陈华[2] 

机构地区：[1]辽宁科技大学材料与冶金学院,辽宁鞍山114051 [2]鞍钢股份有限公司鲅鱼圈分公司,辽宁营口115007

出　　处：《铸造技术》2015年第7期1813-1816,共4页Foundry Technology

基　　金：鞍山市科技计划项目资助(2012000386)

摘　　要：针对当前炉外精炼渣主要成分Ca O在空气中易水化变质的不足,利用可通气间歇反应釜,采用化学包覆法对石灰细粉进行防水化实验研究。实验结果表明:采用反应釜搅拌可大大改善反应动力学条件,加快反应速度,降低反应温度。当实验条件为反应温度300℃,通气时间45 min,通气量3.5 L/min,搅拌速度800 r/min时,氧化钙表面包覆了一层碳酸钙薄膜,样品存放15天,吸水率仅为0.05%,远低于未经表面包覆处理的石灰。Since CaO in refining slag is easy to absorb water in the air, experimental study on hydration resistance of calcium oxide was carried out using batch reactor by chemical cladding. The results show that, when the experimental temperature is 300 ℃, the reaction time is 45 min, gas flow is 3.5 L/min,stirring rate is 800 r/min, the surface of CaO powder is coated with calcium carbonate layer. The calcium oxide water adsorption is only 0.05% after 15 days. It is far below the untreated calcium oxide water adsorption.

关 键 词：钝化 氧化钙 间歇反应釜 吸水率 表面包覆 

分 类 号：TG260[金属学及工艺—铸造] TB306[一般工业技术—材料科学与工程]