水性丙烯酸树脂/氧化石墨烯抗静电涂层的制备及性能研究  

Preparation and Properties Characterization of Waterborne Acrylic Resin/Graphene Oxide Antistatic Coating

作　　者：胡楠[1] 赵丽娟[1] 范靖[1] 胡雪莲[1] 李权[1] 

机构地区：[1]四川师范大学化学与材料科学学院,四川成都610066

出　　处：《塑料工业》2015年第8期91-94,共4页China Plastics Industry

基　　金：国家自然科学基金(51303116)

摘　　要：采用水性丙烯酸树脂为基料,考察了氧化石墨烯含量对抗静电涂层性能的影响。结果表明,当氧化石墨烯质量分数为3.5%时,涂层的体积电阻率达到2.604×107Ω·cm,冲击性能和耐老化性能均最佳。Using waterborne acrylic resin as the basic material, the influence of graphene oxide content on the antistatic coating performance was investigated in this paper. Experimental results showed that the volume resistivity of the coating with graphene oxide content of 3.5% was 2.604×10^7 Ω·cm with the best impact performance and aging resistance.

关 键 词：水性丙烯酸树脂 氧化石墨烯 抗静电 拉伸 耐冲击性 

分 类 号：TQ637[化学工程—精细化工]