覆膜钼粉SLS成型件后处理实验研究  

Study on Post-treated Experiment of SLS Parts After Polymer-coated Molybdenum Powders

作　　者：姜乐涛[1,2] 白培康[1] 赵娜[2] 刘宇琨 

机构地区：[1]中北大学材料科学与工程学院,山西太原030051 [2]石家庄经济学院,河北石家庄050700

出　　处：《热加工工艺》2015年第14期135-138,142,共5页Hot Working Technology

摘　　要：制备了选择性激光烧结用覆膜钼粉,采用用SLS技术制备了成型件。利用真空炉对成型件进行了后处理,并得到了脱脂、预烧结和高温烧结的最佳工艺。对成型件和高温烧结件的微观形貌和力学性能进行了研究。结果表明：最佳工艺为脱脂温度300~400℃,预烧结温度1200~1400℃,高温活化烧结1600℃。高温活化烧结后的成型件物理性能得到很大提高,孔隙率14.5%,体密度6.3 g·cm-3,抗拉强度304.5 MPa,伸长率为7.8%和冲击韧性9.6 k J·m2。Polymer-coated molybdenum powders for selective laser sintering（SLS） process were obtained.Green parts were manufactured with SLS. After the prototyping parts were post-treated in vacuum stove, the best products of polymer removal, pre-sintering and high temperature sintering were obtained.The microstructure and mechanical properties of the prototyping parts and high temperature sintering parts were studied. The conclusions show that： the best optimum process is the polymer removing temperature of 300-400℃, pre-sintering temperature of 1200-1400℃, high temperature sintering temperature of 1600℃. The physical properties of the parts greatly improve, which is that the porosity is 14.5%, the bulk density is 6.3 g·cm-3, the tensile strength is 304.5 MPa, the elongation is 7.8% and the toughness is 9.6 k J·m2.

关 键 词：选择性激光烧结 高温烧结 覆膜钼粉 性能 

分 类 号：TG146.4[一般工业技术—材料科学与工程] TF124[金属学及工艺—金属材料]