WC颗粒增强高铬钢基表面复合材料的滑动摩擦磨损性能研究  

Sliding Friction and Wear Properties of WC Particles Reinforced High Chrome Steel Matrix Surface Composite

作　　者：刘旋[1] 丁克伟[1] 刘运林[1] 

机构地区：[1]安徽建筑大学合肥建筑结构与地下工程安徽省重点实验室,安徽合肥230601

出　　处：《热加工工艺》2015年第14期174-177,共4页Hot Working Technology

基　　金：安徽建筑大学青年专项经费资助

摘　　要：采用真空实型铸渗法(V-EPC)工艺,制备了WC颗粒增强高铬钢基表面复合材料,并研究了载荷、转速对WC颗粒增强高铬钢基表面复合材料和高铬钢滑动摩擦磨损性能的影响。研究结果表明:在不同的转速、载荷的条件下,表面复合材料耐磨性都比高铬钢要优越,其中转速影响更为显著,相对耐磨性从100r/min的2.5(最小值)增大到250 r/min的40.7(最大值)。WC-particles reinforced high chrome steel matrix surface composite materials are prepared by the way of the V-EPC infiltration, and study the effect of the sliding friction and wear properties of high Chrome steel matrix surface composite material and high chrome steel under the load and speed. The results shows that： In different speed or load,Abrasion resistance of the surface composite materials are superior to the high chromium steels, the speed is more obvious, the relative abrasion resistance from 2.5（minimum） of 100 r/min increased to 40.7（max） of 250 r/min.

关 键 词：真空实型铸渗法 WC颗粒 表面复合材料 高铬钢 滑动摩擦磨损 

分 类 号：TB33[一般工业技术—材料科学与工程]