海洋用钢焊接接头的海水腐蚀行为研究  被引量:11

Seawater Corrosion Behavior of Welding Joints of Steels for Marine Applications

在线阅读下载全文

作  者:黄桂桥[1,2] 韩冰[1,2] 杨海洋[1,2] 

机构地区:[1]青岛钢研纳克检测防护技术有限公司,山东青岛266071 [2]钢铁研究总院青岛海洋腐蚀研究所,山东青岛266071

出  处:《装备环境工程》2015年第4期11-15,共5页Equipment Environmental Engineering

摘  要:目的研究海洋用钢焊接接头的海水腐蚀行为。方法采用海水暴露试验、电偶腐蚀试验和腐蚀电位测量等方法。结果获得了5种海洋用钢焊接接头的海水腐蚀结果。结论海洋用钢焊接接头的熔合区易产生腐蚀沟槽。在全浸区、潮差区和飞溅区条件下,同一焊接接头的腐蚀行为相同,焊接接头的腐蚀严重程度顺序为全浸区>潮差区>飞溅区。焊缝-母材的电偶腐蚀试验结果与焊接接头的暴露腐蚀结果一致。Objective To investigate the seawater corrosion behavior of welding joints of steels for marine application. Methods The methods including exposure tests, galvanic corrosion tests and potential measurements were carried out for the study. Results Seawater corrosion results of welding joints of steels for marine application were obtained. Conclusion Corrosion grooves were easily occurred in the fusion zone of welding joints. Corrosion behavior of certain welding joint of the steels is same among full immersion zone, tidal zone and splash zone; the order of localized corrosion degree of is full immersion zone〉 tidal zone〉 splash zone. Results of galvanic corrosion tests of weld metal-base metal are consistent well to the exposure tests of the welding joints in seawater.

关 键 词: 焊接接头 海水 腐蚀 

分 类 号:TJ04[兵器科学与技术—兵器发射理论与技术] TG172.5[金属学及工艺—金属表面处理]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象