水成膜消防泡沫对船舶甲板涂料颜色影响的研究  

Research on Effect of Aqueous Film Forming Foam(AFFF) on Coatings Colors for Ship Deck

作　　者：莫立新[1] 张卫国[2] 崔显林[2] 王同良[2] 成建强[2] 

机构地区：[1]海军驻426厂军事代表室,辽宁大连116000 [2]海洋化工研究院有限公司海洋涂料国家重点实验室,山东青岛266071

出　　处：《中国涂料》2015年第7期55-58,共4页China Coatings

摘　　要：用数字显微镜对水成膜消防泡沫对环氧、聚氨酯甲板涂料的变色影响进行了研究。未经老化的环氧涂料涂膜致密,耐消防泡沫性能较好。老化10个月以上的环氧涂料,表面产生明显老化现象,耐消防泡沫性能大大下降,表面变白并产生细裂纹。The effect of aqueous iflm forming foam on the discoloration of epoxy and polyurethane deck coatings was researched with the digital microscope. The iflm of the epoxy coatings was compact before aging and had preferable AFFF resistance. But after the epoxy coatings were aged for 10 months, aging phenomenon occurred obviously on the surfaces, the AFFF resistance declined signiifcantly and the surface was whitened and with ifne cracks.

关 键 词：水成膜消防泡沫 船舶甲板涂料 颜色 环氧 聚氨酯 