ZTC4/TA2钛合金双金属复合界面的研究  

Study on Interfacial Properties of ZTC4/TA2 Titanium Alloy Bimetal

作　　者：李柱[1] 程序[1] 赵嘉琪[2] 张美娟[2] 南海[2] 吴国清[1] 

机构地区：[1]北京航空航天大学材料科学与工程学院,北京100191 [2]北京航空材料研究院,北京100095

出　　处：《铸造技术》2015年第8期2045-2047,共3页Foundry Technology

基　　金：航空科学基金(2012ZE51056);教育部长江学者和创新团队发展计划(IRT0805)

摘　　要：以ZTC4/TA2钛合金镶嵌管体为研究对象,采用扫描电镜、金相显微镜、显微硬度仪等对复合界面形态及结构进行表征,研究了镶嵌管体表面粗糙度对复合界面的影响。结果表明,经镶铸后TA2镶嵌管体由片状α组成的魏氏体组织组成,ZTC4母材由片层状α片间+β晶界的金相组织。在熔合界面处,形成了Al元素的连续扩散层合金硬度呈平缓过渡,实现了两种合金的冶金结合。随着镶嵌管体表面粗糙度的增加,界面熔合率降低。The interfacial properties of ZTC4/TA2 bimetal castings were studied by SEM, optical microscope and hardness tester. The results show that after bimetal casting, a widmanstatten microstructure of α phase was formed at TA2 alloy side, while an α＋β lamellar microstructure was formed at the ZTC4 alloy side. A continuing Al diffusion zone was found at the ZTC4/TA2 alloy interfacial area with good metallic bonding. The degree of ZTC4 and TA2 alloys fusion degree decrease by increasing the surface roughness of insert tube.

关 键 词：钛合金 双金属复合 镶铸 界面 

分 类 号：TG146.23[一般工业技术—材料科学与工程]