Effect of Multi-axial Compression on Microstructure and Mechanical Properties of 7085 Aluminum Alloy Extrusions

作　　者：莫纪平[1] 程晓农[1] 邓平安[1] 许晓静[1] 吴瑶[1] 蒋伟[1] 

机构地区：[1]江苏大学,江苏镇江212013

出　　处：《稀有金属材料与工程》2015年第8期2003-2006,共4页Rare Metal Materials and Engineering

基　　金：江苏省工业科技支撑计划项目(BE2008118);江苏大学拔尖人才培养工程基金(1211110001);江苏省高校研究生科研创新计划项目(CXLX12-0620)

摘　　要：通过对合金进行X射线衍射(XRD)及电子背散射衍射技术(EBSD)分析、拉伸性能测试,研究了多向压缩对合金组织和力学性能的影响。结果表明:多向压缩可以显著细化合金晶粒(由87.7μm降低到17.9μm),晶粒细化机制主要是动态再结晶;提高抗拉强度110 MPa,合金主要通过时效强化和固溶强化。The effect of multi-axial compression on microstructure and mechanical properties of 7085 aluminum alloy extrusions was investigated by X-ray diffraction（XRD）, electron back-scattered diffraction（EBSD） and tensile test. The results show that multi-axial compression could refine the grain size（from 87.7 μm to 17.9 μm） with the grain refinement mechanism of dynamic recrystallization, increase the tensile strength by 110 MPa which is primarily attributed to solution strengthening and aging strengthening.

关 键 词：7085铝合金 多向压缩 EBSD 晶粒细化 

分 类 号：TG146.21[一般工业技术—材料科学与工程]