LLDPE/EVA/改性MH/MRP阻燃体系的研究  

Study on LLDPE/EVA/Modified MH/MRP Flame Retardant System

作　　者：黄婷[1,2] 凌桂香[1,2] 龙丹[1,2] 

机构地区：[1]贵州省交通规划勘察设计研究院股份有限公司,贵州贵阳550081 [2]山地交通灾害防治技术国家地方联合工程实验室,贵州贵阳550081

出　　处：《塑料科技》2015年第9期38-41,共4页Plastics Science and Technology

基　　金：贵阳市科技计划项目2013工业振兴科技计划(筑科合同[2013101]1-6号)

摘　　要：选用乙烯-醋酸乙烯共聚物/改性氢氧化镁/微胶囊红磷(EVA/改性MH/MRP)为复合阻燃体系,研究体系的力学性能及阻燃性能,并通过扫描电镜观察材料燃烧后炭层的表面形貌。结果表明:当LLDPE/EVA/改性MH/MRP添加比例为60:40:70:10时,拉伸强度为11.3 MPa,断裂伸长率为353%,氧指数为31.4%,垂直燃烧试验通过UL 94V-0级,体系具有良好的阻燃协效作用和力学相容性。The mechanical properties and flame retardant properties of modified EVA/MH/MRP were studied. The surface morphology of carbon layer was observed by scanning electron microscope（SEM）. The results of SEM show that when the LLDPE/EVA/modified MH/MRP adding proportion is 60：40：70：10, the tensile strength is 11.3 MPa, the elongation at break is 353% and the oxygen index（OI） is 31.4%. Vertical burning test reaches to V-0 level, and the system has good flame retardant effect and mechanical compatibility.

关 键 词：线型低密度聚乙烯 改性氢氧化镁 微胶囊红磷 乙烯-醋酸乙烯共聚物 阻燃协效作用 力学相容性 

分 类 号：TQ325.12[化学工程—合成树脂塑料工业]