覆膜Mo粉SLS成形件熔渗金属工艺研究  

Infiltration Treatment of SLS Parts with Polymer-coated Molybdenum Powders

作　　者：姜乐涛[1,2] 白培康[1] 赵娜[2] 刘宇琨 

机构地区：[1]中北大学材料科学与工程学院 [2]石家庄经济学院

出　　处：《特种铸造及有色合金》2015年第8期863-866,共4页Special Casting & Nonferrous Alloys

摘　　要：制备可用于选择性激光烧结成形的覆膜钼粉,并用SLS技术成形了制件。在真空炉中对成形件进行了后处理试验,得到了脱脂、预烧结、渗金属的最佳工艺,制得了符合性能要求的渗铜件。对渗铜件的微观形貌和力学性能进行了研究。结果表明,渗铜件性能得到了明显提高,孔隙率为3.2%,密度为9.68g/cm^3,抗拉强度为480-490 MPa,伸长率为12.1%-12.7%,冲击韧度为14.1-14.8kJ·m^-2。Polymer-coated molybdenum powders for selective laser sintering（SLS）process were produced,and green parts were manufactured by SLS.After the prototyping parts were post-treated in the vacuum furnace,the desirable parameters with polymer removal,pre-sintering and infiltration were presented.The infiltration parts with satisfied mechanical properties were produced successfully.The microstructure and mechanical properties of the infiltration parts were analyzed.The results reveal that the properties of the parts prepared are improved greatly,where the parameters,such as the porosity,the density,tensile strength,the elongation and compact toughness reach 3.2%,9.68g·cm^-3,480-490 MPa,12.1%-12.7% and 14.1-14.8kJ·m^-2,respectively.

关 键 词：覆膜钼粉 选择性激光烧结 熔渗 性能 

分 类 号：TB331[一般工业技术—材料科学与工程] TF124[冶金工程—粉末冶金]