冷轧压下率和退火温度对高强IF钢组织和性能的影响  

Influences of Cold Rolling Reduction Ratio and Annealing Temperature on Microstructure and Mechanical Properties of High Strength IF Steel

作　　者：罗磊[1,2] 赵广彬[1] 郑之旺[2] 王敏莉[2] 

机构地区：[1]西华大学材料科学与工程学院,四川成都610039 [2]攀钢集团研究院有限公司,四川成都611731

出　　处：《热加工工艺》2015年第17期40-43,共4页Hot Working Technology

摘　　要：对不同冷轧压下率（55%、65%、75%、85%）的高强IF钢进行了不同工艺的盐浴退火。研究了冷轧压下率和退火工艺对高强IF钢显微组织和力学性能的影响,确定了最佳冷轧压下率和退火温度范围。结果表明高强IF钢退火温度840-860℃且冷轧压下率65%-75%时,达到较好的强塑性匹配。The high strength IF steel of the different cold rolling reduction ratios （55%, 65%, 75%, 85%） was annealed by salt-bath method with different processes. The effects of cold rolling reduction ratio and annealing temperature on the microstructure and mechanical properties of high strength IF steel were studied. And the annealing temperature range and cold rolling reduction ratio were determined. The results show that high strength IF steel annealing temperatures are 840-860℃ and cold rolling reduction ratios are 65% -75%, which reaches optimal matching of strength and plasticity.

关 键 词：高强IF钢 盐浴退火 冷轧压下率 力学性能 

分 类 号：TG335.13[金属学及工艺—金属压力加工] TG161