Dynamic mechanical analysis of single walled carbon nanotubes/polymethyl methacrylate nanocomposite films  

作　　者：Ali Badawi N.Al-Hosiny 

机构地区：[1]Department of Physics,Faculty of Science,Taif University [2]Department of Physics,Faculty of Science,Aljouf University

出　　处：《Chinese Physics B》2015年第10期331-335,共5页中国物理B（英文版）

基　　金：Project supported by Taif University(Grant No.1/435/3524)

摘　　要：Dynamic mechanical properties of nanocomposite films with different ratios of single walled carbon nanotubes/polymethyl methacrylate（SWCNTs/PMMA） are studied. Nanocomposite films of different ratios（0, 0.5, 1.0, and2.0 weight percent（wt%）） of SWCNTs/PMMA are fabricated by using a casting technique. The morphological and structural properties of both SWCNT powder and SWCNTs/PMMA nanocomposite films are investigated by using a high resolution transmission electron microscope and x-ray diffractometer respectively. The mechanical properties including the storage modulus, loss modulus, loss factor（tan δ） and stiffness of the nanocomposite film as a function of temperature are recorded by using a dynamic mechanical analyzer at a frequency of 1 Hz. Compared with pure PMMA film, the nanocomposite films with different ratios of SWCNTs/PMMA are observed to have enhanced storage moduli, loss moduli and high stiffness, each of which is a function of temperature. The intensity of the tan δ peak for pure PMMA film is larger than those of the nanocomposite films. The glass transition temperature（T g） of SWCNTs/PMMA nanocomposite film shifts towards the higher temperature side with respect to pure PMMA film from 91.2？C to 99.5？C as the ratio of SWCNTs/PMMA increases from 0 to 2.0 wt%.Dynamic mechanical properties of nanocomposite films with different ratios of single walled carbon nanotubes/polymethyl methacrylate（SWCNTs/PMMA） are studied. Nanocomposite films of different ratios（0, 0.5, 1.0, and2.0 weight percent（wt%）） of SWCNTs/PMMA are fabricated by using a casting technique. The morphological and structural properties of both SWCNT powder and SWCNTs/PMMA nanocomposite films are investigated by using a high resolution transmission electron microscope and x-ray diffractometer respectively. The mechanical properties including the storage modulus, loss modulus, loss factor（tan δ） and stiffness of the nanocomposite film as a function of temperature are recorded by using a dynamic mechanical analyzer at a frequency of 1 Hz. Compared with pure PMMA film, the nanocomposite films with different ratios of SWCNTs/PMMA are observed to have enhanced storage moduli, loss moduli and high stiffness, each of which is a function of temperature. The intensity of the tan δ peak for pure PMMA film is larger than those of the nanocomposite films. The glass transition temperature（T g） of SWCNTs/PMMA nanocomposite film shifts towards the higher temperature side with respect to pure PMMA film from 91.2？C to 99.5？C as the ratio of SWCNTs/PMMA increases from 0 to 2.0 wt%.

关 键 词：SWCNTs/PMMA nanocomposite mechanical properties STIFFNESS glass transition temperature 

分 类 号：O484[理学—固体物理]