铌对取向硅钢中沉淀析出的影响  

Effect of Nb on Precipitates in Grain Oriented Silicon Steel

作　　者：冯运莉[1] 尹晓盼 张思佳[1] 

机构地区：[1]河北联合大学冶金与能源学院河北省现代冶金技术重点实验室,河北唐山063009

出　　处：《热加工工艺》2015年第18期89-91,共3页Hot Working Technology

基　　金：国家自然科学基金资助项目(51274083);河北省高等学校创新团队领军人才培育计划(LJRC007);河北省自然科学基金资助项目(E2013209228)

摘　　要：应变诱导析出过程中应力的测量常应用弛豫法,通过Gleeble-3500热模拟试验机,采用应力弛豫试验测定了含Nb和不含Nb取向硅钢的沉淀析出动力学PTT曲线。结果表明PTT曲线均呈现野C冶形,鼻尖温度在900～950℃。含Nb试验钢的PTT曲线比不含铌试验钢的PTT曲线偏左上方,即铌的加入加速了第二相的沉淀析出,缩短了孕育期。The stress-relaxation method was widely used to measure strain-induced precipitation process at high temperature. The precipitation-time-temperature curves of the oriented silicon steel with and without Nb were investigated by stress relaxation method on Gleeble-3500 physical simulator. The results show that PTT curves are like ＇C＇,the shortest precipitation temperature is at 900-950 ℃. The PTT curve of the test steel with Nb is at top left of PTT curve of the test steel without Nb. The addition of Nb can accelerate the precipitation and shorten the incubation time.

关 键 词：取向硅钢 NB 应力弛豫 沉淀析出 PTT 曲线 

分 类 号：TG113.2[金属学及工艺—物理冶金]