轧制宽幅铝箔生产工艺试验研究  

Experimental study on the rolling process of wide width aluminum foil

作　　者：张代录[1,2] 胡世军[1,2] 张红香[1,2] 杨笠 

机构地区：[1]兰州理工大学数字制造技术与应用省部共建教育部重点实验室,甘肃兰州730050 [2]兰州理工大学机电工程学院,甘肃兰州730050 [3]甘肃蓝星清洗技术有限公司,甘肃兰州730050

出　　处：《轻金属》2015年第9期52-54,共3页Light Metals

摘　　要：为了提高宽幅双零箔材的表面质量,通过制定合理的试验方案和拟定轧制工艺参数,反复现场对比试验,分析试验结果,最后确定了轧制宽幅双零铝箔的最佳生产工艺参数。实践证明,所制定的生产工艺合理,且轧制的宽幅双零箔材表面质量明显提高,满足了用户要求。In order to improve the surface quality of double zero aluminum foil with wide width, the best rolling process parameters of double zero aluminum foil with wide width were determined through establishing the reasonable testing scheme and studying out rolling process parameters, contrast test repeatedly and analyzing of test results. The practice had proved that developed production process was reasonably, and rolled surface quality of double zero aluminum foil with wide width was improved obviously, and met the requirements of customers.

关 键 词：轧制 宽幅 铝箔 试验 分析 

分 类 号：TG339[金属学及工艺—金属压力加工]