聚丙烯酸酯核壳粒子的制备及其增韧尼龙6的研究  

Preparation of Polyacrylate Core-shell Structured Particles and Toughening on Nylon 6

作　　者：王润生 马静[2] 姚艳梅[2] 李红蕊[2] 瞿雄伟[2] 

机构地区：[1]山东省青岛五十八中,山东青岛266100 [2]河北工业大学化工学院,天津300130

出　　处：《塑料工业》2015年第10期40-43,47,共5页China Plastics Industry

基　　金：河北省自然科学基金项目(E2010000107)

摘　　要：采用热引发体系,以聚丙烯酸正丁酯为核层,聚甲基丙烯酸甲酯为壳层,并在最外层共聚功能单体甲基丙烯酸,以种子乳液聚合法制备了聚丙烯酸酯核-壳粒子;研究了不同核层交联密度的聚丙烯酸酯对尼龙6的增韧作用。结果表明,在乳液聚合反应中,单体转化率高,聚丙烯酸酯核-壳粒子的结构和组成可控,粒径在295 nm;当核层与壳层聚合物的质量比为85/15,核层交联剂用量和甲基丙烯酸均为单体总质量的0.5%时,尼龙6共混物的缺口冲击强度最高,是纯尼龙的7倍。With poly （n-butyl acrylate ） as core layer, polymethylmethaerylate as shell layer and methylacrylic acid as a functional monomer copolymerized in the outermost shell layer, polyacrylate core-shell structured particles were prepared by seeded emulsion polymerization using thermal initiation system. The toughening effect of polyaerylate with different crosslinking density of the shell layer on nylon 6 was studied. The results indicated that in the emulsion polymerization, the monomer conversion was high, the structure and constituent of polyacrylate core-shell structured particles was controllable, and the particle size reached 295 nm; with the core-shell weight ratio of 85/15 and the contents of the erosslinking agent for the shell layer and methylacrylie acid were 0. 5% of the total monomer mass, the nylon 6 blend had the highest notch impact strength which was almost six times greater than that of pure PA6.

关 键 词：尼龙6 聚丙烯酸酯 核-壳结构 乳液聚合 增韧 

分 类 号：TQ342.11[化学工程—化纤工业]