Preparation of ZSM-5 Coated on Monolithic Interconnected Macroporous Al2O3 Using Cheap n-Butylamine as Template  

作　　者：Mingliang Sun Tianbo Zhao Jia Wang Zhaofei Ma Fengyan Li 

机构地区：[1]Institute for Chemical Physics, Beijing Institute of Technology, Beijing 100081, China [2]Department of Applied Chemistry, Beijing Institute of Petrochemical Technology, Beijing 102617, China

出　　处：《Chinese Journal of Chemistry》2015年第9期1057-1063,共7页中国化学（英文版）

基　　金：This work was supported by tile National Natural Science Foundation of China （Nos. B030301 and A020601） and the State Key Laboratory of Catalytic Materials and Reaction Engineering （RIPP, SINOPEC）.

摘　　要：Using cheap n-butylamine as template, ZSM-5 zeolites have been successfully synthesized and coated on mon- olithic interconnected macroporous Al2O3 by the secondary growth method. The use of cheap n-butylamine could significantly reduce the synthesis cost. Hierarchical monolithic ZSM-5 zeolites were prepared from synthetic mix- tures with different H2O/Na2O or SiO2/Al2O3 ratio. The synthesized samples were characterized by scanning elec- tron microscopy （SEM）, X-ray diffraction （XRD）, Fourier transform infrared spectroscopy （FT-IR） and N2 ad- sorption-desorption. The results show that the hierarchical monolithic zeolites were obtained with cheap n-butylamine template as template. During the hydrothermal reaction process, the morphology of the microme- ter-sized support was well maintained. The irregular crystals were formed in a wide range of the H2O/Na2O or SiO2/Al2O3 ratio of synthetic mixtures and coated on monolithic Al2O3. The relative crystallinity of the zeolites was highest at H2O/Na2O=250 or SiO2/Al2O3= 160. This type of composites exhibited hierarchical porous structures and relatively high specific surface areas.Using cheap n-butylamine as template, ZSM-5 zeolites have been successfully synthesized and coated on mon- olithic interconnected macroporous Al2O3 by the secondary growth method. The use of cheap n-butylamine could significantly reduce the synthesis cost. Hierarchical monolithic ZSM-5 zeolites were prepared from synthetic mix- tures with different H2O/Na2O or SiO2/Al2O3 ratio. The synthesized samples were characterized by scanning elec- tron microscopy （SEM）, X-ray diffraction （XRD）, Fourier transform infrared spectroscopy （FT-IR） and N2 ad- sorption-desorption. The results show that the hierarchical monolithic zeolites were obtained with cheap n-butylamine template as template. During the hydrothermal reaction process, the morphology of the microme- ter-sized support was well maintained. The irregular crystals were formed in a wide range of the H2O/Na2O or SiO2/Al2O3 ratio of synthetic mixtures and coated on monolithic Al2O3. The relative crystallinity of the zeolites was highest at H2O/Na2O=250 or SiO2/Al2O3= 160. This type of composites exhibited hierarchical porous structures and relatively high specific surface areas.

关 键 词：hierarchical MONOLITHIC zeolites template synthesis secondary growth 

分 类 号：TQ424.25[化学工程] TQ174.758