Trap states induced by reactive ion etching in AlGaN/GaN high-electron-mobility transistors  

作　　者：罗俊 赵胜雷 宓珉瀚 侯斌 杨晓蕾 张进成 马晓华 郝跃 

机构地区：[1]Key Laboratory of Wide Band-Gap Semiconductor Materials and Devices, School of Microelectronics, Xidian University [2]School of Advanced Materials and Nanotechnology, Xidian University

出　　处：《Chinese Physics B》2015年第11期460-463,共4页中国物理B（英文版）

基　　金：supported by the National Natural Science Foundation of China(Grant Nos.61334002 and 61106106)

摘　　要：Frequency-dependent conductance measurements were carried out to investigate the trap states induced by reactive ion etching in A1GaN/GaN high-electron-mobility transistors （HEMTs） quantitatively. For the non-recessed HEMT, the trap state density decreases from 2.48 × 1013 cm-2.eV-1 at an energy of 0.29 eV to 2.79 × 1012 cm-2.eV-1 at ET = 0.33 eV. In contrast, the trap state density of 2.38 × 1013-1.10× 1014 cm-2.eV-1 is located at ET in a range of 0.30-0.33 eV for the recessed HEMT. Thus, lots of trap states with shallow energy levels are induced by the gate recess etching. The induced shallow trap states can be changed into deep trap states by 350 ℃ annealing process. As a result, there are two different types of trap sates, fast and slow, in the annealed HEMT. The parameters of the annealed HEMT are ET = 0.29-0.31 eV and DT = 8.16× 1012-5.58 × 1013 cm-2.eV-1 for the fast trap states, and ET = 0.37-0.45 eV and DT = 1.84×1013- 8.50 × 1013 cm-2.eV-1 for the slow trap states. The gate leakage currents are changed by the etching and following annealing process, and this change can be explained by the analysis of the trap states.Frequency-dependent conductance measurements were carried out to investigate the trap states induced by reactive ion etching in A1GaN/GaN high-electron-mobility transistors （HEMTs） quantitatively. For the non-recessed HEMT, the trap state density decreases from 2.48 × 1013 cm-2.eV-1 at an energy of 0.29 eV to 2.79 × 1012 cm-2.eV-1 at ET = 0.33 eV. In contrast, the trap state density of 2.38 × 1013-1.10× 1014 cm-2.eV-1 is located at ET in a range of 0.30-0.33 eV for the recessed HEMT. Thus, lots of trap states with shallow energy levels are induced by the gate recess etching. The induced shallow trap states can be changed into deep trap states by 350 ℃ annealing process. As a result, there are two different types of trap sates, fast and slow, in the annealed HEMT. The parameters of the annealed HEMT are ET = 0.29-0.31 eV and DT = 8.16× 1012-5.58 × 1013 cm-2.eV-1 for the fast trap states, and ET = 0.37-0.45 eV and DT = 1.84×1013- 8.50 × 1013 cm-2.eV-1 for the slow trap states. The gate leakage currents are changed by the etching and following annealing process, and this change can be explained by the analysis of the trap states.

关 键 词：AlGaN/GaN high-electron mobility transistors （HEMTs） ANNEALING reactive ion etching trapstates 

分 类 号：TN386[电子电信—物理电子学]