Two Isostructural Multi-metal Borates: Syntheses, Crystal Structures and Characterizations of M_3LiNa_4Be_4B_(10)O_(24)F(M = Sr, Cd)  

作　　者：王小珊 刘丽娟 夏明军 王晓洋 陈创天 

机构地区：[1]Beijing Center for Crystal Research and Development, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences [2]Graduate University of Chinese Academy of Sciences

出　　处：《Chinese Journal of Structural Chemistry》2015年第10期1617-1625,共9页结构化学（英文）

基　　金：supported by the National Natural Science Foundation of China(No.50972149,61138004,51402316);the National Instrumentation Program(No.2012YQ120048)

摘　　要：Two new isostructural multi-metal beryllium borates, m^3 Li Na4Be4B10O24F（M = Sr（1）, Cd（2））, have been synthesized by spontaneous crystallization. The structures were verified by single-crystal X-ray crystallography. The compounds crystallize in the trigonal space group R 3, with a = b = 9.4645（1） A, c = 38.842（8） A, V = 3013.2（6） A3, Z = 6, F（000） = 2568, Dc = 3.005 g/cm^3, Mr = 908.9, R = 0.0327, w R = 0.0678, μ = 8.160 mm-1 for Sr3 Li Na4Be4B10O24F and a = b = 9.3019（8） A, c = 37.782（7） A, V = 2831.12（9） A3, Z = 6, F（000） = 2748, Dc = 3.459 g/cm^3, Mr = 983.24, R = 0.0158, w R = 0.0455, μ = 3.586 mm-1 for Cd3 Li Na4Be4B10O24F. The structures are characterized by an infinite two-dimensional [Be8B16O40F2]∞ double layer bridged by [B12O24] groups like a sandwich structure, while the cations reside in tunnels along different directions. UV-vis-IR diffuse reflectance spectroscopy demonstrates that their cut-off edges are below 200 nm. Thermal analysis shows that they melt incongruently and their melting points are around 740-770 ℃.Two new isostructural multi-metal beryllium borates, m^3 Li Na4Be4B10O24F（M = Sr（1）, Cd（2））, have been synthesized by spontaneous crystallization. The structures were verified by single-crystal X-ray crystallography. The compounds crystallize in the trigonal space group R 3, with a = b = 9.4645（1） A, c = 38.842（8） A, V = 3013.2（6） A3, Z = 6, F（000） = 2568, Dc = 3.005 g/cm^3, Mr = 908.9, R = 0.0327, w R = 0.0678, μ = 8.160 mm-1 for Sr3 Li Na4Be4B10O24F and a = b = 9.3019（8） A, c = 37.782（7） A, V = 2831.12（9） A3, Z = 6, F（000） = 2748, Dc = 3.459 g/cm^3, Mr = 983.24, R = 0.0158, w R = 0.0455, μ = 3.586 mm-1 for Cd3 Li Na4Be4B10O24F. The structures are characterized by an infinite two-dimensional [Be8B16O40F2]∞ double layer bridged by [B12O24] groups like a sandwich structure, while the cations reside in tunnels along different directions. UV-vis-IR diffuse reflectance spectroscopy demonstrates that their cut-off edges are below 200 nm. Thermal analysis shows that they melt incongruently and their melting points are around 740-770 ℃.

关 键 词：borates [B12O24] group optical material sandwich structure multi-metal 

分 类 号：O611.4[理学—无机化学]