用于染料敏化太阳能电池的多壁碳纳米管基对电极的制备与表征(英文)  

Fabrication and characterization of a multi-walled carbon nanotube-based counter electrode for dye-sensitized solar cells

作　　者：郑威[1] 齐涛[1] 张永超[1] 石海英[1] 田均庆 

机构地区：[1]哈尔滨理工大学材料科学与工程学院,黑龙江哈尔滨150040

出　　处：《新型炭材料》2015年第5期391-396,共6页New Carbon Materials

基　　金：哈尔滨市科技创新人才项目(2013RFXXJ004)~~

摘　　要：经酸化处理的多壁碳纳米管(MWCNTs)与纳米石墨复合后沉积在FTO导电玻璃基底上制备出染料敏华太阳能电池薄膜对电极。利用SEM、TEM、EDS与IR光谱对其进行表征。以Mg O掺杂的Ti O2薄膜为光阳极对电池通过循环伏安法(CV曲线)、电化学阻抗谱(EIS)和伏安特性曲线(J-V)进行光电性能分析。结果表明:酸化处理的MWCNTs与纳米石墨复合对电极展现出优异的光催化性能,有利于电池光电性能的提高。电池开路电压及短路电流密度分别可达0.53 V、4.67 m A/cm2,其光电转换效率达到4.10%,与铂对电极的性能相当。A counter-electrode （CE） for dye-sensitized solar cells （DSSCs） was prepared by coating a slurry containing acid-oxi- dized multi-wall carbon nanotubes and nano-graphite powder onto a fluorine-doped tin oxide conducting glass substrate. The samples were characterized by SEM, TEM, EDS and IR spectroscopy. The CE performance in the DSSCs with MgO-doped TiO2 as the pho- toanode was investigated by measurements of current-voltage curves, cyclic voltammetry and electrochemical impedance spectrosco- py. Results show that the cell with the CE exhibits the best photoelectric properties of all the carbon-based CEs investigated. The short-circuit current density （ Jsc ） is 4.67 mA/cm2 , the open-circuit voltage （ Voc ） is 0.53 V and photoelectric conversion efficiency is up to 4.10%, which are comparable with those of the Pt-based CE in DSSCs.

关 键 词：染料敏化太阳能电池 对电极 多壁碳纳米管 石墨 光催化活性 

分 类 号：TM914.4[电气工程—电力电子与电力传动]