冷镦钢线材冷顶锻开裂问题分析及改善措施  

Analysis on & Improvement Measures of Cold Forging Cracking of Cold Heading Steel Wire

作　　者：刘春林[1] 农之江 张志明 

机构地区：[1]北京科技大学冶金与生态工程学院,北京100083 [2]宝钢集团广东韶关钢铁有限公司,广东韶关512100

出　　处：《南方金属》2015年第6期30-33,共4页Southern Metals

摘　　要：冷镦钢是用来加工紧固件的钢铁材料.紧固件加工过程最容易出现的质量问题是镦头开裂,墩头开裂主要原因是线材的缺陷.文章结合实践经验,对冷镦钢线材冷顶锻开裂和产生此类质量缺陷的原因进行分析,并采取相应的改进,使顶锻开裂得以改善.Cold heading steel is the steel materials for processing fastening pieces. The common quality problems of pro- cessing the fastening pieces are prone to cold forging cracking which was mainly caused by the heredity of wire defects. The problems of cold forging cracking of cold heading steel wire and the causes are stated, the countermeasures and methods for reducing the cracking are given, which help reduce the defect rate.

关 键 词：冷镦钢 顶锻开裂 表面质量 夹杂 组织 