YPO_4:Dy^(3+),Eu^(3+)荧光粉的水热合成及白光发射  

Hydrothermal preparation and white-light emission of YPO_4:Dy^(3+),Eu^(3+) phosphors

作　　者：霍涌前[1] 于本武 陈小利[1] 王艳妮[1] 任岗[1] 张瑾[1] 张谋真[1] 刘晓莉[1] 

机构地区：[1]延安大学化学与化工学院,陕西延安716000

出　　处：《光电子．激光》2015年第11期2141-2147,共7页Journal of Optoelectronics·Laser

基　　金：国家自然科学基金(21101133)资助项目

摘　　要：采用水热法,合成了YPO 4:xDy^(3+),0.06Eu^(3+)系列荧光粉。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、电子散射能谱(EDS)、光致发光(PL)谱和长余辉光谱,分别对样品的物相、结构和PL进行了表征。XRD检测表明,合成的样品属四方晶系;荧光光谱测试表明,在234nm紫外光激发下,YPO4:xDy^(3+),0.06Eu^(3+)的发射光谱呈现Eu^(3+)的5 D7 0→7 F1(592nm,橙光)和5 D0→F2(618nm,红光)的发光峰;而在354nm的激发波长下,YPO^(3+)4 4:0.06Dy,0.06Eu^(3+)的发射光谱呈现Dy^(3+)的F9/2→6 H615/2(486nm、蓝光)和4 F9/2→H13/2(575nm、黄光)的发光峰,以及Eu^(3+)的5 D0→7 F1(592nm、橙光)和5 D0→7 F2(619nm、红光)的发光峰。对荧光衰减谱的双参数拟合证实了Dy^(3+)→Eu^(3+)能量传递的存在。色坐标图显示,在234nm紫外光激发下,YPO4:0.05Dy^(3+),0.06Eu^(3+)是很好的近紫外光激发下的白色荧光粉。The YPO4：xDy^3＋,0.06Eu^3＋phosphors were synthesized by hydrothermal method.The prepared products were studied by X-ray powder diffraction（XRD）,scanning electron microscopy（SEM）,energy dispersive spectrometer（EDS）,photoluminescence（PL）spectroscopy and long-lasting phosphorescence.The results by XRD indicate that YPO4：0.05Dy^3＋,0.06Eu^3＋belongs to a tetragonal crystal system.Photoelectron spectroscopy measurement from YPO4：0.05Dy^3＋,0.06Eu^3＋reveals the binding energy of the elements onto the product surfaces.When excited by 234 nm,the characteristic emission peaks of Eu^3＋due to the transitions of 5 D0→7 F1 at 592nm and 5 D0→7 F2 at 618nm were observed in the emission spectra of YPO4：xDy^3＋,0.06Eu^3＋.The emission spectra of YPO4：0.06Dy^3＋,0.06Eu^3＋excited by 354 nm are composed of blue（4 F9/2→6 H15/2,486nm）and yellow（4 F9/2→6 H13/2,575nm）emission peaks of Dy^3＋,orange（5 D0→7 F1,592nm）and red（5 D0→7 F2,619nm）emission peaks of Eu^3＋,and white light emission can be observed.The energy transfer is confirmed to occur between Dy^3＋and Eu^3＋when the decay spectrum of Dy^3＋is fitted by a double-exponential function.From Commission Internationale de L′Eclairage（CIE）chromaticity diagram,it is noted that white light can be achieved in the emission spectra of YPO4：0.05Dy^3＋,0.06Eu^3＋phosphor at 234 nm excitation.

关 键 词：YPO4:Dy3+ Eu3+ 发光材料 白光 水热合成 

分 类 号：O611.65[理学—无机化学]