塑料薄膜表面化学镀镍工艺的研究  

Research on Electroless Nickel Plating Technology on the Surface of Plastic Films

作　　者：崔培英[1] 

机构地区：[1]曲阜师范大学化学与化工学院,山东曲阜273165

出　　处：《辽宁化工》2015年第12期1445-1447,共3页Liaoning Chemical Industry

摘　　要：实验研究了塑料薄膜表面化学镀镍的操作方法、控制条件,讨论了各种因素对镀层质量的影响,确定了塑料薄膜化学镀镍的工艺流程和最佳实验条件。实验结果表明,塑料薄膜经过预处理及敏化、活化处理后,化学镀镍溶液的p H值控制在5.5,镀镍温度在60℃,反应时间35 min,可以得到较好的塑料薄膜化学镀镍镀层。The operating methods and condition of electroless nickel plating on surface of the plastic films were studied; influence of several factors on nickel-plating on the surface of the plastic films was discussed. The best process and optimum conditions were finally determined. The results show that the optimum conditions are as follows： p H=5.5, the nickel plating temperature 60℃ and the reaction time 35 min.Under above condition, good nickel-plating coating on surface plastic films after pretreatment, sensitization and activation can be gained.