一体化SOFC多孔YSZ电极基体性能优化  

Optimization of Porous YSZ Substrate in the Tri-layer Structure Solid Oxide Fuel Cell

作　　者：杨志宾[1] 张敏[1] 林志成[1] 赵鹏[1] 朱腾龙[1] 郑紫微[1] 韩敏芳[1,2] 

机构地区：[1]中国矿业大学(北京)燃料电池中心,北京100083 [2]清华大学热能工程系,北京100084

出　　处：《硅酸盐学报》2016年第1期1-5,共5页Journal of The Chinese Ceramic Society

基　　金：国家"973"计划资助项目(2012CB215404);山西省煤基重点科技攻关项目(MD2014-08);国家自然科学基金项目(51402355);北京市自然科学基金项目(2154056)

摘　　要：研究了阳极支撑一体化电池Y_2O_3稳定ZrO_2(YSZ)基体孔隙率对电导率和力学性能的影响,分析了不同孔隙率下YSZ基体的孔结构,优化出最佳孔隙率(65.8%)的YSZ基体。在此基础上,通过浸渍工艺制备了标准尺寸阳极支撑一体化SOFC。测试结果表明,750℃最大功率密度达0.35 W/cm^2。The conductivity and bending strength of Y203 stabilized ZrO2 （YSZ） ceramic substrates with different porosities were investigated. The pore structure of YSZ with different porosities was analyzed, and the optimized porosity of 65.8% was obtained. Anode supported tri-layer single cell with the standard size was fabricated via impregnation technique. The results show that the maximum power density of the cell can be 0.35 W/cm2 at 750℃.

关 键 词：固体氧化物燃料电池 一体化 多孔结构 钇稳定氧化锆 孔分布 

分 类 号：TQ174.1[化学工程—陶瓷工业]