基于磁性Fe3O4/Ag的表面增强拉曼光谱检测农药丙线磷  

Detection of Ethoprophos Using SERS Coupled with Magnetic Fe_3O_4/Ag Composite Materials

作　　者：袁荣辉[1] 刘文涵[1] 滕渊洁[1] 聂晶[1] 马苏珍 

机构地区：[1]浙江工业大学化学工程学院,绿色化学合成技术国家重点实验室培育基地,浙江杭州310032

出　　处：《光谱学与光谱分析》2015年第5期1276-1280,共5页Spectroscopy and Spectral Analysis

基　　金：国家自然科学基金项目(10804099);上海市功能性材料化学重点实验室开放课题项目(SKLFMC2013C01);浙江省公益性技术应用研究(分析测试)计划项目(2014C37044)资助

摘　　要：以共沉淀法合成Fe3O4纳米颗粒,再通过柠檬酸三钠还原AgNO3制备Fe3O4/Ag磁性复合材料。Fe3O4/Ag能够与溶液中的丙线磷形成吸附,通过磁性收集达到萃取富集的效果。测定吸附于Fe3O4/Ag表面的痕量丙线磷所产生的表面增强拉曼光谱(SERS),其检测过程的拉曼增强因子为1.48×105,极大地提高了检测灵敏度,建立了磁性Fe3O4/Ag萃取富集与SERS分析农药丙线磷的方法。采用紫外可见吸收光谱、能谱及透射电子显微镜对制备的材料进行了分析及形貌与结构的表征。并对丙线磷模型分子进行结构优化的密度泛函理论计算,得到了理论拉曼光谱和谱峰归属,以用于丙线磷的判断。结果表明,SERS峰强在富集15min后基本趋于稳定,其丙线磷浓度低至2×10-8 mol·L-1仍有明显响应,可以满足丙线磷农残检测的要求。其方法可推广至含硫有机磷农药残留的分析。The magnetic Fe3O4/Ag composite materials were synthesized by reducing AgNO3 with sodium citrate in the presence of Fe3O4 which were prepared by co-precipitation firstly.The enrichment and extraction of ethoprophos assembled on Fe3O4/Ag were achieved with the applied magnetic field.The different concentrations of ethoprophos adsorbed on Fe3O4/Ag were analyzed by SERS and it was showed that the trace analysis of ethoprophos had been established,while the enhancement factor of probe molecules on Fe3O4/Ag was 1.48×10^5.The structure and morphology of Fe3O4/Ag were characterized by UV-Vis,EDX and TEM.Compared with Ag,the UV-Vis absorption peak of Fe3O4/Ag shifted from 417 to 369nm,and the UV-Vis of Fe3O4 almost had no characteristic absorption peak in this region.At the same time,it was showed that the surface properties of Fe3O4/Ag changed with Raman enhancement effect during the aggregation process of Ag around the surface of Fe3O4.Further EDX images of micro area element analysis suggested that the chemical composition of products were Ag,Fe and O while the Cu peak was from the copper mesh.In addition,TEM images indicated that the average particle size of Fe3O4 was between 30 and 60nm with shape tended to be spherical.And the silver nanoparticles were attached to the Fe3O4 particles and agglomeration occured.Density functional theory calculations which can be applied to qualitative judgment of molecule was carried out to obtain the molecular optimization structure and theoretical Raman spectra.It was found that the stabilized SERS signals were detected under the saturated adsorption equilibrium after 15 min.Finally,Raman response of ethoprophos was achieved with lower than 2×10^-8 mol·L^-1,indicatint that the established method had reached the requirements of ethoprophos residues detection and could be used for analysis of sulfur-containing organophosphorus pesticide.

关 键 词：Fe3O4/Ag 磁性复合材料 表面增强拉曼光谱 丙线磷 

分 类 号：O657[理学—分析化学]