pH和Cl^-对Cu-Cr-Zr合金电化学腐蚀的影响  

Effect of pH and Cl^- on Electrochemical Corrosion of Cu-Cr-Zr Alloy

作　　者：陈小娜[1] 张修庆[1] 程小敏[1] 陈舸[1] 丁昱寰 

机构地区：[1]华东理工大学机械与动力工程学院,上海200237

出　　处：《腐蚀与防护》2015年第1期49-53,共5页Corrosion & Protection

基　　金：上海市自然科学基金(12ZR1407400)

摘　　要：采用电化学方法研究了Cu-Cr-Zr合金在不同pH条件下含0.6mol/L的NaCl和纯水溶液中的耐蚀性,采用扫描电子显微镜(SEM)、能谱(EDS)表征了浸泡试验72h后试样的表面形貌。将其在不同腐蚀介质中的耐电化学腐蚀性作对比,结果表明,Cl-的加入使合金在同等pH条件下的耐蚀性下降;碱性环境降低了Cl-对合金的腐蚀;在强酸溶液中合金会发生全面均匀的腐蚀,在强碱溶液中合金发生局部腐蚀。Eelectrochemical methods were applied to study the corrosion resistance of Cu-Cr-Zr alloy under the condition of 0.6mol/L NaCl solution and pure water solutions with different pH.The structure and morphology of samples after 72 hours immersion tests were characterized by SEM and EDS.Corrosion resistance of samples in different solutions were compared.The results showed that the corrosion resistance of Cu-Cr-Zr alloy was decreased by chloride ions.The electrochemical corrosion of Cu-Cr-Zr alloy in the chlorine solution decreased in the alkaline environment,uniform corrosion occurred in strong acid solution,and localized corrosion occurred in strong alkaline solution.

关 键 词：CU-CR-ZR合金 NACL溶液 电化学 腐蚀 

分 类 号：TG174[金属学及工艺—金属表面处理]