微弧离子沉积阻燃涂层及其性能  

Study on performance of burn-resistant coating deposited by micro-arc ion surface modification technology

作　　者：傅斌友[1] 汪瑞军[1] 史萌[1] 屈轶[1] 

机构地区：[1]北京金轮坤天特种机械有限公司,北京100083

出　　处：《焊接学报》2015年第6期19-22,114,共4页Transactions of The China Welding Institution

基　　金：国防装备预先研究资助项目(AT010201023W1)

摘　　要：采用微弧离子表面改性技术在TC11合金表面制备阻燃涂层,采用扫描电镜、透射电镜、XRD等方法分析了阻燃涂层组织及物相,采用＂钛火＂液滴法试验平台测试了TC11钛合金在300~700℃之间的燃烧参数,验证了同等试验条件下带有阻燃涂层TC11钛合金试样在300~700℃之间的阻燃有效性.结果表明,制备的阻燃涂层主要由Ti Zr非晶相组成,涂层致密,与基体为冶金结合,700℃以内具有一定的阻燃性能,分析阻燃涂层的阻燃机理主要为涂层吸收能量,减小基体对热量的吸收,同时阻止钛合金与氧接触机制来阻燃.Burn-resistant coatings were deposited on TC11 titanium alloys by Micro-arc ion surface modification technology.The SEM,TEM and the X-ray diffraction technologies were employed to analyze microstructure and phases of the coating. The combustion parameters of TC11 titanium alloys and the fire-resistant performance of the coatings were measured by titanium fire melt liquid-drop method experimental rig. The results showed that the coating contained TiZ r amorphous phases and displayed rather dense,while the serviceability temperature under 700 ℃ the coating had fire-resistant performance. The burnresistant coatings absorbed energy,and reduced energy which absorbed by substrate. In the same time,these coatings prevent titanium alloy from meeting oxygen.

关 键 词：微弧离子表面改性技术 阻燃涂层 TC11钛合金 阻燃性能 

分 类 号：TG434[金属学及工艺—焊接]